Melt-stable semi-crystalline lactide polymer film and process for manufacture thereof

ABSTRACT

A film having a net endotherm greater than about 10 joules per gram of polymer that contains chains including lactic acid residuals; said film further comprising; a) a melt stable polymer composition comprising at least 5% by weight of a melt stable first polymer component with lactic acid residuals b) said first polymer having a number average molecular weight of at least 40,000 and no greater than 300,000 and c) said first melt stable polymer composition having a lactide concentration of less than about 2% by weight of melt stable polymer including polymer chains with lactic acid residuals. A process for preparing a film having a net endotherm greater than about 10 joules per gram of polymer that contains chains including lactic acid residuals is also disclosed.

CROSS REFERENCE TO RELATED APPLICATIONS

The present application is a continuing application of application Ser. No. 08/110,394 filed Aug. 23, 1993, and which issued as U.S. Pat. No. 5,536,807 on Jul. 16, 1996. Application Ser. No. 08/110,394 is a continuation-in-part of application Ser. No. 07/955,690 filed Oct. 2, 1992, and which issued as U.S. Pat. No. 5,338,822 on Aug. 16, 1994. The disclosures of application Ser. No. 08/110,394 and application Ser. No. 07/955,690 are incorporated herein by reference.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to a semi-crystalline film comprising a melt-stable, biodegradable, lactide polymer composition and a process for manufacturing the film from a melt-stable, biodegradable polymer.

2. Description of the Prior Art

The need for polymeric biodegradable films is well established. Films manufactured from blown or cast processes are well known. Typically in a blown film process, a plastic melt passes through a die which extrudes the molten plastic into an annular shape. Typically, the extruded film is extruded in an upward fashion. As the film moves upward, air is blown into the film which expands the film into a tubular shape. The tube is generally closed at some distance above the die, with a pair of nip rolls.

In a cast film process, a sheet is typically extruded from a slit die. The sheet is thereafter pulled through a series of rollers which cool the extruded sheet and may also elongate the length and width of the sheet to a desired dimension and thickness.

The use of films is widespread and well known in the art. The heaviest use of films occurs in the packaging and disposable article industries. Films employed in the packaging industry include films used in food and non-food packaging, merchandise bags and trash bags. In the disposable article industry, the general use occur in the construction of diapers and personal hygiene articles, including tapes.

In light of depleting landfill space and adequate disposal sites, there is a need for biodegradable films. Currently, films comprising polymers such as polyethylene, polypropylene, polyethylene terephthlate, nylon, polystyrene, polyvinyl chloride and polyvinylidene chloride are popular for their superior extrusion and film-making properties. However, these films are not biodegradable. Furthermore, these films are generally noncompostable, which is undesirable from an environmental point of view.

Films have been developed which are generally considered to be biodegradable. These are films which purportedly have adequate properties to permit them to break down when exposed to conditions which lead to composting. Examples of such arguably biodegradable films include those made from polycaprolactone, starch biopolymers and polyvinyl alcohol.

Although films extruded from these materials have been employed in film containing articles, many problems have been encountered with their use. Often the films are not completely biodegradable or compostable. Furthermore, some biodegradable films may also be unduly sensitive; to water, either limiting the use of the film or requiring some type of surface treatment to the film, often rendering the film nonbiodegradable. Others have inadequate heat resistance for wide spread use. Thus, there is a need for a film which is completely biodegradable.

The present invention recognizes the importance of crystallinity and further introduces methods to achieve such crystallinity.

The use of lactic acid and lactide to manufacture a biodegradable polymer is known in the medical industry. As disclosed by Nieuwenhuis et al. (U.S. Pat. No. 5,053,485), such polymers have been used for making biodegradable sutures, clamps, bone plates and biologically active controlled release devices. Processes developed for the manufacture of polymers to be utilized in the medical industry have incorporated techniques which respond to the need for high purity and biocompatability in the final product. These processes were designed to produce small volumes of high dollar-value products, with less emphasis on manufacturing cost and yield.

In order to meet projected needs for biodegradable packaging materials, others have endeavored to optimize lactide polymer processing systems. Gruber et al. (U.S. Pat. No. 5,142,023) disclose a continuous process for the manufacture of lactide polymers with controlled optical purity from lactic acid having physical properties suitable for replacing present petrochemical-based polymers.

Generally, manufacturers of polymers utilizing processes such as those disclosed by Gruber et al. will convert raw material monomers into polymer beads, resins or other pelletized or powdered products. The polymer in this form may then be sold to end users who convert, i.e., extrude, blow-mold, cast films, blow films, thermoform, injection-mold or fiber-spin the polymer at elevated temperatures to form useful articles. The above processes are collectively referred to as melt-processing. Polymers produced by processes such as those disclosed by Gruber et al., which are to be sold commercially as beads, resins, powders or other non-finished solid forms are generally referred to collectively as polymer resins.

Prior to the present invention, it is believed that there has been no disclosure of a combination of composition control and melt stability requirements which will lead to the production of commercially viable, semi-crystalline lactide polymer film.

It is generally known that lactide polymers or poly(lactide) are unstable. The concept of instability has both negative and positive aspects. A positive aspect is the biodegradation or other forms of degradation which occur when lactide polymers or articles manufactured from lactide polymers are discarded or composted after completing their useful life. A negative aspect of such instability is the degradation of lactide polymers during processing at elevated temperatures as, for example, during melt-processing by end-user purchasers of polymer resins. Thus, the same properties that make lactide polymers desirable as replacements for non-degradable petrochemical polymers also create undesirable effects during processing which must be overcome.

Lactide polymer degradation at elevated temperature has been the subject of several studies, including: I. C. McNeill and H. A. Leiper, Polymer Degradation and Stability, vol. 11, pp. 267-285 (1985); I. C. McNeill and H. A. Leiper, Polymer Degradation and Stability, vol. 11, pp. 309-326 (1985); M. C. Gupta and V. G. Deshmukh, Colloid & Polymer Science, vol. 260, pp. 308-311 (1982); M. C. Gupta and V. G. Deshmukh, Colloid & Polymer Science, vol. 260, pp. 514-517 (1982); Ingo Luderwald, Dev. Polymer Degradation, vol. 2, pp. 77-98 (1979); Domenico Garozzo, Mario Giuffrida, and Giorgio Montaudo, Macromolecules, vol. 19, pp. 1643-1649 (1986); and, K. Jamshidi, S. H. Hyon and Y. Ikada, Polymer, vol. 29, pp. 2229-2234 (1988).

It is known that lactide polymers exhibit an equilibrium relationship with lactide as represented by the reaction below: ##STR1##

No consensus has been reached as to what the primary degradation pathways are at elevated processing temperatures. One of the proposed reaction pathways includes the reaction of a hydroxyl end group in a "back-biting" reaction to form lactide. This equilibrium reaction is illustrated above. Other proposed reaction pathways include: reaction of the hydroxyl end group in a "back-biting" reaction to form cyclic oligomers, chain scission through hydrolysis of the ester bonds, an intramolecular beta-elimination reaction producing a new acid end group and an unsaturated carbon-carbon bond, and radical chain decomposition reactions. Regardless of the mechanism or mechanisms involved, the fact that substantial degradation occurs at elevated temperatures, such as those used by melt-processors, creates an obstacle to use of lactide polymers as a replacement for petrochemical-based polymers. It is apparent that degradation of the polymer during melt-processing must be reduced to a commercially acceptable rate while the polymer maintains the qualities of biodegradation or compostability which make it so desirable. It is believed this problem has not been addressed prior to the developments disclosed herein.

As indicated above, poly(lactide)s have been produced in the past, but primarily for use in medical devices. These polymers exhibit biodegradability, but also a more stringent requirement of being bioresorbable or biocompatible. As disclosed by M. Vert, Die Ingwandte Makromolekulare Chemie, vol. 166-167, pp. 155-168 (1989), "The use of additives is precluded because they can leach out easily in body fluids and then be recognized as toxic, or, at least, they can be the source of fast aging with loss of the properties which motivated their use. Therefore, it is much more suitable to achieve property adjustment through chemical or physical structure factors, even if aging is still a problem." Thus, work aimed at the bioresorbable or biocompatible market focused on poly(lactide) and blends which did not include any additives.

Other disclosures in the medical area include Nieuwenhuis (European Patent No. 0 314 245), Nieuwenhuis (U.S. Pat. No. 5,053,485), Eitenmuller (U.S. Pat. No. 5,108,399), Shinoda (U.S. Pat. No. 5,041,529), Fouty (Canadian Patent No. 808,731), Fouty (Canadian Patent No. 923,245), Schneider (Canadian Patent No. 863,673), and Nakamura et al., Bio. Materials and Clinical Applications, Vol. 7, p. 759 (1987). As disclosed in these references, in the high value, low volume medical specialty market, poly(lactide) or lactide polymers and copolymers can be given the required physical properties by generating lactide of very high purity by means of such methods as solvent extraction or recrystallization followed by polymerization. The polymer generated from this high purity lactide is a very high molecular weight product which will retain its physical properties even if substantial degradation occurs and the molecular weight drops significantly during processing. Also, the polymer may be precipitated from a solvent in order to remove residual monomer and catalysts. Each of these treatments add stability to the polymer, but clearly at a high cost which would not be feasible for lactide polymer compositions which are to be used to replace inexpensive petrochemical-based polymers in the manufacture of films.

Furthermore, it is well-known that an increase in molecular weight generally results in an increase in a polymer's viscosity. A viscosity which is too high can prevent melt-processing of the polymer due to physical/mechanical limitations of the melt-processing equipment. Melt-processing of higher molecular weight polymers generally requires the use of increased temperatures to sufficiently reduce viscosity so that processing can proceed. However, there is an upper limit to temperatures used during processing. Increased temperatures increase degradation of the lactide polymer, as the previously-cited studies disclose

Jamshidi et al., Polymer, Vol. 29, pp. 2229-2234 (1988) disclose that the glass transition temperature of a lactide polymer, T_(g), plateaus at about 57° C. for poly(lactide) having a number average molecular weight of greater than 10,000. It is also disclosed that the melting point, T_(m), of poly (L-lactide) levels off at about 184° C. for semi-crystalline lactide polymers having a number average molecular weight of about 70,000 or higher. This indicates that at a relatively low molecular weight, at least some physical properties of lactide polymers plateau and remain constant.

Sinclair et al. (U.S. Pat. No. 5,130,765) disclose the use of residual monomer, lactic acid or lactic acid oligomers to plasticize poly(lactide) polymers, with plasticizer levels of 2-60 percent. Loomis (U.S. Pat. No. 5,076,983) discloses a process for manufacturing a self-supporting film in which the oligomers of hydroxy acids are used as plasticizing agents. Loomis and Sinclair et al. disclose that the use of a plasticizer such as lactide or oligomers of lactic acid is beneficial to produce more flexible materials which are considered to be preferable. Sinclair et al., however, disclose that residual monomer can deposit out on rollers during processing. Loomis also recognizes that excessive levels of lactide or oligomers of lactic acid can cause unevenness in films and may separate and stick to and foul processing equipment. Thus, plasticizing as recommended, negatively impacts melt-processability in certain applications.

Accordingly, a need exists for a lactide polymer which is melt-stable under the elevated temperatures common to melt-processing resins in the manufacture of film. The needed melt-stable polymer composition must also exhibit sufficient compostability or degradability after its useful life as a film. Further, the melt-stable polymer must be processable in existing melt-processing equipment, by exhibiting sufficiently low viscosities at melt-processing temperatures while polymer degradation and lactide formation remains below a point of substantial degradation and does not cause excessive fouling of processing equipment. Furthermore, the lactide polymer must retain its molecular weight, viscosity and other physical properties within commercially-acceptable levels through the film manufacturing process. The present invention also offers further advantages over the prior art, and solves other problems the prior art, and solves other problems associated therewith.

SUMMARY OF THE INVENTION

According to the present invention, a semi-crystalline poly(lactide) film exhibiting a net melting endotherm greater than about 10 joules per gram is provided. The semi-crystalline poly(lactide) film comprises a melt-stable, lactide polymer composition comprising: a plurality of poly(lactide) polymer chains, the polymer being a reaction product of polymerizing a lactide mixture comprising less than about 15 percent by weight meso-lactide. The remaining lactide can be L-lactide, D-lactide or mixtures thereof provided that the overall lactide mixture comprises at least about 85% of either the L or D lactide isomer. This area is shown in FIG. 4. The polymer has residual lactide in a concentration of less than about 2 percent by weight; and water in a concentration of less than about 2,000 parts per million. A process for the manufacture of the film is also provided. For the purposes of the present invention, the film may be manufactured from any number of methods and is not to be limited by the particular method.

Optionally, stabilizing agents in the form of anti-oxidants and water scavengers may be added. Further, plasticizers, nucleating agents, anti-static agents, slip aids and anti-blocking agents may be added. The resultant film is biodegradable and may be disposed of in an environmentally sound fashion.

Poly(lactide) is a polymeric material which offers unique advantages as a film not only in the biodegradable sense, but in the manufacturing process as well.

The present invention describes a method of increasing the degree of crystallinity in a film or sheet by drawing the film in a machine and/or transverse direction orientation at temperatures near the Tg. The Tg can be lowered to near room temperature through the use of plasticizers.

Strain hardening is a phenomenon which, if present, can be used to obtain high quality, uniform, semi-crystalline films. A description of strain hardening in stretching of films of poly(ethylene 2,6, naphthalene dicarboxilate) is given by Cakmak et al. M. Cakmak, Y. D. Wang, and M. Simhambhatla, Polymer Engineering and Science, June 1990, Vol. 30, p 721-733!. Strain hardening can be identified by an increase in the force required to continue elongation of a film. The essential feature of this phenomenon is the appearance of necks (thin areas) during the stretching operation. High amounts of stretching occurs locally in the necked region, causing it to elongate more than the surrounding areas. The elongation presumably causes the further crystallization of the previous "weak" neck. A neck elsewhere in the film then forms, elongates, crystallizes, hardens and increases its resistance to further elongation. This continues until all areas of the film have once again reached a uniform thickness. As shown by Cakmak et al., the process results in very smooth, high quality films.

We have observed necking in poly(lactide) as it has been subjected to stress induced crystallization, and believe that strain hardening may be occurring. The films which have stretched often feel smoother to the touch, although no surface profiling tests have been done. The films of the present invention may be used in articles such as diapers, packaging film, agricultural mulch film, bags and tape.

The films of the present invention are superior in diaper constructions as compared to other films such as polypropylene or polyethylene. The typical construction of a diaper comprises an outer, water impervious back sheet, a middle absorbent layer and an inner layer. The outer back sheet, comprising the exterior of the diaper, is desirable from an environmental point of view if it is biodegradable. The film of the present invention satisfies this environmental concern by being biodegradable and compostable.

Furthermore, a poly(lactide) film, unlike other biodegradable polymers, is believed to not support microbial growth during storage and typical film use. Starch or other biodegradable polymers, when exposed to warm, damp environments, will promote the growth of unhealthy microbes. This is undesirable in most personal hygiene products. Thus, the present invention has yet another advantage over prior biodegradable polymers.

Another advantage of the present invention is the high surface energy of poly(lactide) films. Poly(lactide) is a material with a relatively high surface energy, when compared to other films. As the surface energy of an extruded film increases, the driving force to remain intact and to minimize surface area increases, therefore the tendency to form a smooth, coherent, high gloss film increases. A high surface energy film also has the advantage of having a surface which is easier to print on. This is an important feature in packaging applications and diapers.

The film of the present invention exhibits a higher surface energy than untreated polyolefin films. In order to produce a satisfactory printing surface, these films must first be modified. This not only increases the costs associated with production of the films, but the modification treatment will diffuse into the film and will produce an unsatisfactory printing surface.

The surface energy of substantially pure poly(lactide) films of the present invention is about 44 dynes/cm. This leads to a surface with satisfactory printing characteristics without surface modification. Slip aids or other additives may reduce the surface energy down to about 35 dynes/cm. Additionally, inks which are typically more difficult to apply onto films, like water based inks, may be applied directly to poly(lactide).

Poly(lactide) is a relatively low viscosity polymer which allows the extrusion of the film to be done at lower temperatures than traditional films. This results in a cost savings to the converter because the extrusion equipment will not require as much power when run at lower temperatures.

Heat sealability is also a property of films which is desirable. Poly(lactide) can be heat sealed at temperatures lower than 70° C., at line pressures lower than 40 psi, and at times less than 2 sec.

It has been found that to improve certain properties for poly(lactide), it may be advantageous to blend a second polymer with poly(lactide). The polymer chosen for blending with poly(lactide) will be one which has the properties necessary for the particular need and is compatible with poly(lactide) to the extent that the particular properties of poly(lactide) are improved. Incompatibility often results in a polymer blend which has inferior properties, such as very low tensile strength and modulus. Properties which may be increased include elongation, heat resistance, rheological properties, degradability, impact resistance, tear resistance and barrier properties to oxygen, moisture, or carbon dioxide.

Polymer Blends

To improve certain properties of poly(lactide), it may be advantageous to blend a second polymer with poly(lactide). The polymer chosen for blending with poly(lactide) will be one which has the properties necessary for the particular need and is compatible with of poly(lactide) are improved. Incompatibility often results in a polymer blend which has inferior properties, such as very low tensile resistance, rheological properties, degradability, and barrier properties to oxygen, moisture or carbon dioxide. Polymers which may be useful for improving the film properties of poly(lactide) include aliphatic polyesters or polyamides made by both ring opening and condensation polymerization, esterified cellulose resins, derivitized starch, polyvinylacetate and any of its partially hydrolyzed products including polyvinylalcohol, polyethers including poly(ethylene oxide), polycarbonates, polyurethanes including those based on aliphatic isocyanates, polyanhydrides, natural rubber and its derivatives including epoxidized natural rubber, block copolymers of styrene and isoprene or butadiene and the hydrogenated version of those polymers, polyacrylates and methacrylates, polyolefins, and polystyrene.

Examples of particular interest include polymers which are also degradable including poly(caprolactone), poly(hydroxybutyrate hydroxyvalerate), cellulose acetate, cellulose acetate butyrate, cellulose acetate propionate, and poly(vinyl alcohol).

These polymers may be blended with poly(lactide) in percentages of 1 to 95% by weight to make films of improved properties as shown in Example 1.

The above described features and advantages along with various other advantages and features of novelty are pointed out with particularity in the claims of the present application. However, for a better understanding of the invention, its advantages, and objects attained by its use, reference should be made to the drawings which form a further part of the present application and to the accompanying descriptive matter in which there is illustrated and described preferred embodiments of the present invention.

BRIEF DESCRIPTION OF THE DRAWINGS

In the drawings, in which like reference numerals indicate corresponding parts or elements of preferred embodiments of the present invention throughout the several views;

FIG. 1 is a schematic representation of a preferring process for the manufacture of a melt-stable lactide polymer composition; and

FIG. 2 is a graph showing the equilibrium relationship between lactide and poly(lactide) at various temperatures.

FIG. 3 is a graph showing the melting endotherm for annealed samples of poly(lactide).

FIG. 4 is a phase diagram for meso-lactide, L-lactide and D-lactide.

DETAILED DESCRIPTION OF THE PREFERRED EMBODIMENT(S)

The lactide polymer compositions used in films disclosed herein focus on meeting the requirements of the melt-processor of a lactide polymer resin such as that produced from a process disclosed by Gruber et al. However, the present invention is directed to a poly(lactide) film and is not limited to the lactide polymer composition or process of Gruber et al. Any lactide polymer composition, which comes within the scope of this invention, may be used as a film. As disclosed herein, the problems of degradation, fouling, and lactide formation during melt-processing of lactide polymers are addressed through suggested ranges of molecular weights and compositional limits on impurities such as residual monomer, water and catalyst along with the use of stabilizing agents and catalyst-deactivating agents.

In general, according to the present invention, a melt-stable lactide polymer film and a process for manufacturing a melt-stable lactide polymer film from a melt-stable lactide polymer are disclosed. The use of the term "film" includes not only film, but sheets as well. Lactide polymers are useful due to their recycleable and biodegradable nature. Furthermore, lactide polymers are compostable as illustrated in Example 15 below. Applicants believe the hydrolysis of the ester may be the key to or the first step in degradation of a lactide polymer composition. The mechanism of degradation is not key to the films of the present invention, however it must be recognized that such degradation makes lactide polymers desirable as replacements for presently-utilized non-degradable petrochemical-based polymers used for films.

Applicants have found that the instability of lactide polymers which leads to the beneficial degradation discussed above also creates processing problems. These processing problems include generation of lactide monomer at elevated temperatures and loss in molecular weight believed due to chain scission degradation of the ester bonds and other depolymerization reactions which are not completely understood. No consensus has been reached as to what are the primary degradation pathways at elevated processing temperatures. As previously disclosed, these may include such pathways as equilibrium-driven depolymerization of lactide polymers to form lactide and chain scission through hydrolysis of the ester bonds along with other pathways. For purposes of the present invention, the exact mechanism of degradation at elevated temperatures is not critical.

It is to be understood, however, that degradation of lactide polymers is both beneficial and detrimental. Benefits derive from degradability when articles manufactured from such polymers are discarded. The same or similar types of degradation are detrimental if they occur during processing or prior to the end of the article's useful life.

Lactic acid has two optical isomers, L-lactic acid, also known as (S)-lactic acid, and D-lactic acid, also known as (R)-lactic acid. Three forms of lactide can be derived from the two forms of lactic acid. They are L,L-lactide, also known as L-lactide and which comprises two (S)-lactic acid residuals; D,D-lactide, also known as D-lactide and which comprises two (R)-lactic acid residuals; and meso-lactide, which comprises one each of (R)- and (S)-lactic acid residuals. A 50/50 said mixture of D-lactide and L-lactide with a melting point of about 126° C. is sometimes called D,L-lactide. At temperatures higher than the melting point, it is essentially a liquid mixture of D-lactide and L-lactide.

The similarities and differences between poly(lactic acid) and various poly(lactide)s can best be examined by looking at the distribution of (R) and (S)-lactic acid residuals in the polymers. An L-lactide or D-lactide will introduce a pair of (S) or (R) residuals into the chain, respectively. Meso-lactide introduces an (R,S) or (S,R) dyad. The characteristics of the final polymer will depend for various applications, on the sequencing of the (R) and (S) residuals.

Crystallinity requires relatively long sequences of a particular residual, either long sequences of (R) or of (S). The length of the interrupting sequences may be important for establishing other features of the polymer, such as the rate at which it crystallizes or the melting point of the crystalline phase, or melt processability. The table below shows the expected statistical distribution of the major and minor sequence lengths assuming random polymerization and neglecting transesterification. The table shows data for mixtures containing predominately the (S) configuration, the same results would be obtained for mixtures containing predominately the (R) configuration.

    ______________________________________                                                        Probability  Probability                                                       major sequence                                                                              minor sequence                                                    having length                                                                               having length                                             Optical at least n = at least n =                                       Monomer mix                                                                             Composition                                                                              6      10   20   1    2    3                                ______________________________________                                         Lactic Acid                                                                    95 L/5 D 95 S/5 R  0.77   0.63 0.38 1.0  0.05 0.002                            90 L/10 D                                                                               90 S/10 R 0.59   0.39 0.14 1.0  0.10 0.01                             Lactide                                                                        95 L/5 D 95 S/5 R  0.90   0.81 0.63 1.0  1.0  0.05                             90 L/10 D                                                                               90 S/10 R 0.81   0.66 0.39 1.0  1.0  0.10                             85 L/15 D                                                                               85 S/15 R 0.72   0.52 0.23 1.0  1.0  0.15                             80 L/20 D                                                                               80 S/20 R 0.64   0.41 0.13 1.0  1.0  0.20                             95 L/5 meso                                                                             97 S/3 R  0.88   0.79 0.61 1.0  0.01 0.00                             90 L/10 meso                                                                            95 S/5 R  0.77   0.62 0.37 1.0  0.02 0.00                             85 L/15 meso                                                                            92 S/8 R  0.67   0.48 0.21 1.0  0.04 0.00                             80 L/20 meso                                                                            90 S/10 R 0.57   0.37 0.12 1.0  0.05 0.00                             ______________________________________                                    

The table above shows, that for the L-lactide system, D-lactide or meso-lactide result in similar major sequence lengths at similar levels. The major sequence length is believed to dominate whether or not crystallization can occur. Fischer et al. Fischer, E. W., Sterzel, H. J., and Wegner, G., Kolloid-Z. u.Z Polymere 251, p980-990 (1973)! studied the system of L-lactide and D-lactide and reported that crystallization did not occur if the minor component was more than 15% of the polymerization mixture. Our results, documented in Example 24, show that polymers made of L-lactide and meso-lactide will not crystallize when the polymerization mixture contains more than about 15% of the meso-lactide. These results are consistent with the table above, and suggest that a lactide or lactic acid polymer is crystallizable provided that there is at least a 0.5 probability that sequences of the major conformation comprise at least 10 lactic acid residuals.

The table above also shows that polymers of predominately L-lactide with either D-lactide or meso-lactide as minor components have dramatically different sequences of the minor component. For polymers made of L-lactide and meso-lactide there is no chance of having three or more (R)-lactic acid residuals in a row, and a very low probability of having two in a row. For polymers made of L-lactide with low concentrations of D-lactide, the (R)-lactic acid residuals always appear in at least a sequence of length two, with a significant fraction appearing as sequences of length four.

Polymers made either from L- and D-lactic acid (by direct condensation, for example) or from L-lactide with small amounts of meso-lactide have a somewhat similar structure when compared at similar levels of (S) and (R) residuals, as shown in the table above.

Melt-Processing

It is believed that a manufacturer of lactide polymers from a lactide monomer will produce a lactide polymer resin which is in the form of beads or pellets. The melt-processor will convert the resin to a film by elevating the temperature of the resin above at least its glass transition temperature but normally higher and extruding the resin into a film. It is to be understood that the conditions of elevated temperature used in melt-processing cause degradation of lactide polymers during processing. Degradation under melt-processing conditions is shown experimentally in Example 7 based on equilibrium, Example 10 based on catalyst concentration, Example 11 based on catalyst activity, Example 13 based on use of stabilizers and Example 14 based on moisture content. As can be seen in these examples, it is understood that several factors appear to affect the rate of degradation during melt-processing. Applicants have addressed these factors in a combination of compositional requirements and the addition of stabilizing or catalyst-deactivating agents to result in a polymer of lactide which is melt-stable.

In addition, melt-processing frequently produces some proportion of trimmed or rejected material. Environmental concerns and economical efficiencies dictate that this material be reused, typically by regrinding and adding back the material into the polymer feed. This introduces additional thermal stress on the polymer and increases the need for a melt-stable polymer composition.

Melt Stability

The lactide polymers of the present invention are melt-stable. By "melt-stable" it is meant generally that the lactide polymer, when subjected to melt-processing techniques, adequately maintains its physical properties and does not generate by-products in sufficient quantity to foul or coat processing equipment. The melt-stable lactide polymer exhibits reduced degradation and/or reduced lactide formation relative to known lactide polymers. It is to be understood that degradation will occur during melt-processing. The compositional requirements and use of stabilizing agents as disclosed herein reduces the degree of such degradation to a point where physical properties are not significantly affected by melt-processing and fouling by impurities or degradation by-products such as lactide does not occur. Furthermore, the melt-stable polymer should be melt-processable in melt-processing equipment such as that available commercially. Further, the polymer will preferably retain adequate molecular weight and viscosity. The polymer should preferably have sufficiently low viscosity at the temperature of melt-processing so that the extrusion equipment may create an acceptable film. The temperature at which this viscosity is sufficiently low will preferably also be below a temperature at which substantial degradation occurs.

Polymer Composition

The melt-stable lactide polymer film of the present invention comprises a plurality of poly(lactide) polymer chains having a number average molecular weight from about 10,000 to about 300,000. In a preferred composition for a film, the number average molecular weight ranges from about 20,000 to about 275,000. In the most preferred composition, the number average molecular weight ranges from about 40,000 to about 250,000.

In the present invention, a film is considered to be semi-crystalline if it exhibits a net melting endotherm of greater than about 10 J/gm of poly(lactide) when analyzed by a differential scanning calorimeter DSC. To determine whether a film is semi-crystalline it can be tested in a differential scanning calorimeter (DSC), such as marketed by Mettler. An accurately weighed sample of the film, weighing between 5 mg and 15 mg, is placed in the test ampule. A suitable temperature program is to start at -20° C. and scan at 20° C./min to 200° C. Typical features which may be observed include a glass transition at a temperature designated Tg, a relaxation endotherm peak immediately following Tg, a crystallization exotherm peak (generally in the range of 70°-140° C.), and a melting endotherm peak (generally in the range of 100°-200° C.). In the present invention, a film is considered to be semi-crystalline if it exhibits a net melting endotherm of greater than about 10 J/gm of poly(lactide). The net melting endotherm is the energy of the melting endotherm less the energy of the crystallization exotherm if present.

As detailed in Example 9, it appears that the physical properties such as modulus, tensile strength, percentage elongation at break, impact strength, flexural modulus, and flexural strength remain statistically constant when the lactide polymer samples are above a threshold molecular weight. As detailed in Example 22, there is a practical upper limit on molecular weight based on increased viscosity with increased molecular weight. In order to melt-process a high molecular weight lactide polymer, the melt-processing temperature must be increased to reduce the viscosity of the polymer. As pointed out in the Examples, the exact upper limit on molecular weight must be determined for each melt-processing application in that required viscosities vary and residence time within the melt-processing equipment will also vary. Thus, the degree of degradation in each type of processing system will also vary. Based on the disclosure of Example 22, it is believed that one could determine the suitable molecular weight upper limit for meeting the viscosity and degradation requirements in any application.

Lactide polymers can be in either an essentially amorphous form or in a semi-crystalline form. For various applications it will be desirable to have the polymer in semi-crystalline form. Semi-crystalline films have superior heat resistance. The tendency of films to adhere together at temperatures experienced during manufacture, use, shipping or storage when on a roll or part of a product is reduced for semi-crystalline films.

Semi-crystalline films also have decreased permeation to gases, such as oxygen, and moisture. This is an advantage in packaging applications, especially food packaging.

Lactide polymer films with increased crystallinity generally degrade more slowly than amorphous films under conditions of high humidity and heat which results in extended shelf life of the films.

The desired range of compositions for semi-crystalline poly(lactide) is less than about 15 percent by weight meso-lactide and the remaining percent by weight being either L-lactide or D-lactide, wherein at least 85 percent comprises either the L or D-lactide isomer. A more preferred composition contains less than about 12 percent by weight meso-lactide and a most preferred composition has less than about 9 percent by weight meso-lactide with the remainder being substantially all L-lactide and/or D-lactide.

Addition of even small amounts of meso-lactide to the polymerization mixture results in a polymer which is slower to crystallize than polymerization mixtures having lesser amounts of meso-lactide, as detailed in Example 23. Beyond about 15 percent meso content the polymer remains essentially amorphous following the annealing procedure of Example 24.

There are four main methods to increase the rate of crystallization. One is to increase chain mobility at low temperatures, by adding, for example, a plasticizing agent. Dioctyl adipate is an example of a plasticizer which helps crystallization rates in poly(lactide), as detailed in Example 25. A second method to increase the rate of crystallization is to add a nucleating agent, as detailed in Example 26. A third method to induce crystallinity is to orient the polymer molecules. Orientation can be accomplished by drawing during film casting, blowing films, stretching a sheet after it is cast or blown (in multiple directions, if desired), or by the flow of polymer through a small opening in a die. When the process of orientation results in crystallization it is known as stress induced crystallization. This phenomena is illustrated for poly(lactide) in Examples 31 and 32. A fourth method of inducing crystallization is heat-setting, which involves holding a constrained oriented film or fiber at temperatures above Tg. It is demonstrated in Examples 27 and 33. Heat setting involves exposing the film to elevated temperatures, as shown in Plastics Extrusion Technology, F. Hensen (ed), Hanser Publishers, New York, 1988, pp 308, 324. It is preferred to heat set the film under tension to reduce shrinkage during the setting process.

It has been found that poly(lactide) having a meso-content of less than about 12% may be drawn just above its Tg in a machine direction orientation (MDO) or transverse direction orientation (TDO) process to increase the degree of crystallinity. In instances where the Tg of the composition is below room temperature, such as compositions containing at least 15% plasticizer, the sheet may be drawn at room temperature to increase levels of crystallinity from less than 5 J/gm to greater than 15 J/gm. Example 31 demonstrates the increase in crystallinity of a plasticized poly(lactide) sheet upon drawing. The properties of the crystallized and plasticized film are superior with regard to flexible film over non crystallized film. Crystallizing a plasticized film increases the blocking temperature of the film as shown in Example 32. The tensile strength and barrier properties will also increase upon crystallization.

Crystallizing lactide polymer films may be performed by drawing the film in either the machine direction or transverse direction or in both directions using draw ratios of 1.1 or greater. The temperature of the draw rolls are generally set at temperatures at or slightly above the Tg of the film.

The degree of crystallinity in lactide polymer films containing at least 15% plasticizer may also be increased by storing the film at room temperature until levels of crystallinity greater than 10 J/g is reached. Storing the film under elevated temperatures may increase the rate of crystallization, especially in lactide polymer films containing less than 15% plasticizer.

Crystallization of the lactide polymer may also be done during the manufacture of resin pellets. The crystalline portions of the polymer are melted during film manufacture, therefore recrystallization during film manufacture is still required from semi-crystalline films. However, crystalline resin pellets may be dried at higher temperatures, therefore faster than amorphous resin pellets due to the increased resistance of semi-crystalline resin pellets to adhere together at elevated temperatures. Crystallization of the resin pellets may be done by drawing the strand of polymer to a draw ratio of at least 1.1 as it exits the extruder and prior to being pelletized. Crystallinity may also be increased in lactide polymers containing at least 15% plasticizer by storing the pellets at room temperature for a period of time necessary to increase crystallinity above 10 Joules per gram.

Crystalline poly L-lactide exhibits an endotherm of roughly 92 joules per gram at its melting temperature of 170°-190° C., as shown by S. Gogolewski and A. J. Pennings, J Applied Polymer Science, Vol. 28, pp 1045-1061 (1983). The melting point changes with composition. The degree of crystallinity is roughly proportional to the endotherm on melting. For purposes of the present invention, semi-crystalline poly(lactide) exhibits a net melting endotherm above about 10 joules per gram of poly(lactide). For this invention, an amorphous or non-crystalline poly(lactide) is a poly(lactide) or lactide polymer which exhibits a net melting endotherm of less than about 10 joules per gram of poly(lactide) in the temperature range of about 100°-200° C.

The molecular weight of a polymer sample can be determined through the use of gel permeation chromatography (GPC). In the present case, the GPC analysis was conducted with an Ultrastyragel® column from Waters Chromatography. The mobile phase was chloroform. A refractive index detector with molecular weight calibration using polystyrene standards was used. The GPC temperature was 35° C. Molecular weights were determined by integrating from the highest molecular weight fraction down to 4,000 amu. The region below 4,000 amu is excluded from the calculations of molecular weight in order to improve reproducibility of the number average molecular weight. This material may be separately reported as "oligomers" and residual lactide, as in Example 11.

The residual monomer concentration in the melt-stable lactide polymer composition is less than about 2.0 percent by weight. In a preferred composition, the lactide concentration is less than about 1.0 percent by weight and a most preferred composition has less than about 0.5 percent by weight of lactide. Contrary to disclosures in the art, Applicants have found that the monomer cannot be used as a plasticizing agent in the resin of the present invention due to significant fouling of the extrusion equipment. As detailed in Example 16, it is believed the low levels of monomer concentration do not plasticize the final polymer.

The water concentration within the melt-stable lactide polymer composition is less than about 2,000 parts-per-million. Preferably this concentration is less than 500 parts-per-million and most preferably less than about 100 parts-per-million. As detailed in Example 14, the polymer melt-stability is significantly affected by moisture content. Thus, the melt-stable polymer of the present invention must have the water removed prior to melt-processing. Applicants recognize that water concentration ay be reduced prior to processing the polymerized lactide to a resin. Thus, moisture control could be accomplished by packaging such resins in a manner which prevents moisture from contacting the already-dry resin. Alternatively, the moisture content may be reduced at the melt-processor's facility just prior to the melt-processing step in a dryer. Example 14 details the benefit of drying just prior to melt-processing and also details the problems encountered due to water uptake in a polymer resin if not stored in a manner in which moisture exposure is prevented or if not dried prior to melt-processing. As detailed in these examples, Applicants have found that the presence of water causes excessive loss of molecular weight which may affect the physical properties of the melt-processed polymer.

In a preferred composition of the present invention, a stabilizing agent is included in the polymer formulation to reduce degradation of the polymer during production, devolatilization, drying and melt processing by the end user. The stabilizing agents recognized as useful in the present films may include antioxidants and/or water scavengers. Preferred antioxidants are phosphite-containing compounds, hindered phenolic compounds or other phenolic compounds. The antioxidants include such compounds as trialkyl phosphites, mixed alkyl/aryl phosphites, alkylated aryl phosphites, sterically hindered aryl phosphites, aliphatic spirocyclic phosphates, sterically hindered phenyl spirocyclics, sterically hindered bisphosphonites, hydroxyphenyl propionates, hydroxy benzyls, alkylidene bisphenols, alkyl phenols, aromatic amines, thioethers, hindered amines, hydroquinones and mixtures thereof. As detailed in Example 13, many commercially-available stabilizing agents have been tested and fall within the scope of the present melt-stable lactide polymer film. Biodegradable antioxidants are particularly preferred.

The water scavengers which may be utilized in preferred embodiments of the melt-stable lactide polymer film include: carbodiimides, anhydrides, acyl chlorides, isocyanates, alkoxy silanes, and desiccant materials such as clay, alumina, silica gel, zeolites, calcium chloride, calcium carbonate, sodium sulfate, bicarbonates or any other compound which ties up water. Preferably the water scavenger is degradable or compostable. Example 19 details the benefits of utilizing a water scavenger.

In a preferred composition of the present invention, a plasticizer is included in the polymer formulation to improve the film quality of the lactide polymer. More particularly, plasticizers reduce the melt viscosity at a given temperature of poly(lactide), which assists in processing and extruding the polymer at lower temperatures and may improve flexibility and reduce cracking tendencies of the finished film and also improves impact and tear resistance of the film and decreases noise.

A plasticizer is useful in concentration levels of about 1 to 40 percent based on weight of polymer. Preferably, a plasticizer is added at a concentration level of about 5 to 25 percent. Most preferably, a plasticizer is added at a concentration level of about 8 to 25 percent.

Selection of a plasticizing agent requires screening of many potential compounds and consideration of several criteria. For use in a biodegradable film the preferred plasticizer is to be biodegradable, non-toxic and compatible with the resin and relatively nonvolatile.

Plasticizers in the general classes of alkyl or aliphatic esters, ether, and multi-functional esters and/or ethers are preferred. These include alkyl phosphate esters, dialkylether diesters, tricarboxylic esters, epoxidized oils and esters, polyesters, polyglycol diesters, alkyl alkylether diesters, aliphatic diesters, alkylether monoesters, citrate esters, dicarboxylic esters, vegetable oils and their derivatives, and esters of glycerine. Most preferred plasticizers are tricarboxylic esters, citrate esters, esters of glycerine and dicarboxylic esters. Citroflex A4® from Morflex is particularly useful. These esters are anticipated to be biodegradable. Plasticizers containing aromatic functionality or halogens are not preferred because of their possible negative impact on the environment.

For example, appropriate non-toxic character is exhibited by triethyl citrate, acetyltriethyl citrate, tri-n-butyl citrate, acetyltri-n-butyl citrate, acetyltri-n-hexyl citrate, n-butyltri-n-hexyl citrate and dioctyl adipate. Appropriate compatibility is exhibited by acetyltri-n-butyl citrate and dioctyl adipate. Other compatible plasticizers include any plasticizers or combination of plasticizers which can be blended with poly(lactide) and are either miscible with poly(lactide) or which form a mechanically stable blend. Corn oil and mineral oil were found to be incompatible when used alone with poly(lactide) because of phase separation (not mechanically stable) and migration of the plasticizer.

Volatility is determined by the vapor pressure of the plasticizer. An appropriate plasticizer must be sufficiently non-volatile such that the plasticizer stays substantially in the resin formulation throughout the process needed to produce the film. Excessive volatility can lead to fouling of process equipment, which is observed when producing films by melt processing poly(lactide) with a high lactide content. Preferred plasticizers should have a vapor pressure of less than about 10 mm Hg at 170° C., more preferred plasticizers should have a vapor pressure of less than 10 mm Hg at 200° C. Lactide, which is not a preferred plasticizer, has a vapor pressure of about 40 mm Hg at 170° C. Example 6 highlights useful plasticizers for the present invention.

Internal plasticizers, which are bonded to the poly(lactide) may also be useful. Epoxides provide one method of introducing an internal plasticizer.

In a preferred composition, nucleating agents may be incorporated during polymerization. Nucleating agents may include selected plasticizers, finely divided minerals, organic compounds, salts of organic acids and imides and finely divided crystalline polymers with a melting point above the processing temperature of poly(lactide). Examples of useful nucleating agents include talc, sodium salt of saccharin, calcium silicate, sodium benzoate, calcium titanate, boron nitride, copper phthalocyanine, isotactic polypropylene, crystalline poly(lactide) and polybutylene terephthalate.

In a preferred composition, fillers may be used to prevent blocking or sticking of layers or rolls of the film during storage and transport. Inorganic fillers include clays and minerals, either surface modified or not. Examples include talc, diatomaceous earth, silica, mica, kaolin, titanium dioxide, perlite, and wollastonite. Preferred inorganic fillers are environmentally stable and non-toxic.

Organic fillers include a variety of forest and agricultural products, either with or without modification. Examples include cellulose, wheat, starch, modified starch, chitin, chitosan, keratin, cellulosic materials derived from agricultural products, gluten, nut shell flour, wood flour, corn cob flour, and guar gum. Preferred organic fillers are derived from renewable sources and are biodegradable. Fillers may be used either alone or as mixtures of two or more fillers. Examples 4 and 5 highlight useful anti-blocking fillers for the present invention. Surface treatments such as corona and flame treatments may also be used to reduce blocking.

Pigments or color agents may also be added as necessary. Examples include titanium dioxide, clays, calcium carbonate, talc, mica, silica, silicates, iron oxides and hydroxides, carbon black and magnesium oxide.

In the manufacture of the melt-stable lactide polymer compositions of the present invention, the reaction to polymerize lactide is catalyzed. Many catalysts have been cited in literature for use in the ring-opening polymerization of lactones. These include but are not limited to: SnCl₂, SnBr₂, SnCl₄, SnBr₄, aluminum alkoxides, tin alkoxides, zinc alkoxides, SnO, PbO, Sn (2-ethyl hexanoates), Sb (2-ethyl hexanoates), Bi (2-ethyl hexanoates), Na (2-ethyl hexanoates) (sometimes called octoates), Ca stearates, Mg stearates, Zn stearates, and tetraphenyltin. Applicants have also tested several catalysts for polymerization of lactide at 180° C. which include: tin(II) bis(2-ethyl hexanoate) (commercially available from Atochem, as Fascat 2003, and Air Products as DABCO T-9), dibutyltin diacetate (Fascat 4200®, Atochem), butyltin tris(2-ethyl hexanoate) (Fascat 9102®, Atochem), hydrated monobutyltin oxide (Fascat 9100®, Atochem), antimony triacetate (S-21, Atochem), and antimony tris(ethylene glycoxide) (S-24, Atochem). Of these catalysts, tin(II) bis(2-ethyl hexanoate), butyltin tris(2-ethyl hexanoate) and dibutyltin diacetate appear to be most effective.

Applicants have found the use of catalysts to polymerize lactide significantly affects the stability of the resin product. It appears the catalyst as incorporated into the polymer also is effective at catalyzing the reverse depolymerization reaction. Example 10 details the effect of residual catalyst on degradation. To minimize this negative effect, in a preferred composition, the residual catalyst level in the resin is present in a molar ratio of initial monomer-to-catalyst greater than about 3,000:1, preferably greater than about 5,000:1 and most preferably greater than about 10,000:1. Applicants believe a ratio of about 20,000:1 may be used, but polymerization will be slow. Optimization of catalyst levels and the benefits associated therewith are detailed in Example 20. Applicants have found that when the catalyst level is controlled within these parameters, catalytic activity is sufficient to polymerize the lactide while sufficiently low to enable melt-processing without adverse effect when coupled with low residual monomer level and low water concentration as described above in polymers of molecular weight between 10,000 to about 300,000. It is believed in most applications the addition of a stabilizing agent may be unnecessary if the catalyst level is optimized.

Applicants have also found that catalyst concentration may be reduced subsequent to polymerization by precipitation from a solvent. Example 21 demonstrates potential catalyst removal by precipitation from a solvent. This produces a resin with reduced catalyst concentration. In an alternative embodiment, the catalyst means for catalyzing the polymerization of lactide to form the poly(lactide) polymer chains which was incorporated into the melt-stable lactide polymer composition during polymerization is deactivated by including in the melt-stable lactide polymer composition a catalyst deactivating agent in amounts sufficient to reduce catalytic depolymerization of the poly(lactide) polymer chains. Example 11 details the benefits of utilizing a catalyst deactivating agent. Such catalyst-deactivating agents include hindered, alkyl, aryl and phenolic hydrazides, amides of aliphatic and aromatic mono- and dicarboxylic acids, cyclic amides, hydrazones and bishydrazones of aliphatic and aromatic aldehydes, hydrazides of aliphatic and aromatic mono- and dicarboxylic acids, bis-acylated hydrazine derivatives, and heterocyclic compounds. A preferred metal deactivator is Irganox® MD1024 from Ciba-Geigy. Biodegradable metal deactivators are particularly preferred.

In an alternative embodiment, the catalyst concentration is reduced to near zero by utilizing a solid-supported catalyst to polymerize lactide. The feasibility of utilizing such a catalyst is detailed in Example 8. It is believed catalysts which may be utilized include supported metal catalysts, solid acid catalysts, acid clays, alumina silicates, alumina, silica and mixtures thereof.

In a preferred composition, the catalyst usage and/or deactivation is controlled to reduce depolymerization of the poly(lactide) polymer during melt-processing to less than about 2 percent by weight generation of lactide from a devolatilized sample in the first hour at 180° C. and atmospheric pressure. More preferably, the amount of lactide generated is less than about 1 percent by weight in the first hour and most preferably less than about 0.5 percent by weight in the first hour.

A preferred melt-stable lactide polymer composition is the reaction product of polymerization of lactide at a temperature greater than about 160° C. Applicants have found that polymerization at higher temperatures result in a characteristically different polymer which is believed to have improved melt stability due to increased transesterification during polymerization. The benefits of higher temperature polymerization are detailed in Example 12.

Melt-Stable Lactide Polymer Process

The process for the manufacture of a melt-stable lactide polymer comprises the steps of first providing a lactide mixture wherein the mixture contains less than 15 percent by weight meso-lactide with the remainder being L-lactide and/or D-lactide. Such purified lactide stream may be such as that produced in the process disclosed by Gruber et al., although the source of lactide is not critical to the present invention.

The lactide mixture is polymerized to form a lactide polymer or poly(lactide) with some residual unreacted monomer in the presence of a catalyst means for catalyzing the polymerization of lactide to form poly(lactide). Catalysts suitable for such polymerization have been listed previously. The concentration of catalysts utilized may be optimized as detailed in the following examples and discussed previously.

In a preferred embodiment, a stabilizing agent, which may be an antioxidant and/or a water scavenger is added to the lactide polymer. It is recognized that such stabilizing agents may be added simultaneously with or prior to the polymerization of the lactide to form the lactide polymer. The stabilizing agent may also be added subsequent to polymerization.

As previously disclosed, the catalyst usage is adjusted and/or deactivation agent is added in a sufficient amount to reduce depolymerization of poly(lactide) during melt-processing to less than 2 percent by weight generation of lactide from a devolatilized sample in the first hour at 180° C. and atmospheric pressure. More preferably, the stabilizing agent controls lactide generation to less than 1 percent by weight and most preferably less than 0.5 percent by weight in the first hour at 180° C. and atmospheric pressure. Alternatively, the control of catalyst concentration to optimize the balance between necessary catalytic activity to produce poly(lactide) versus the detrimental effects of catalytic depolymerization or degradation of the lactide polymer may be utilized to obviate the need for adding a stabilizing agent.

The lactide polymer is then devolatilized to remove unreacted monomer which may also be a by-product of decomposition reactions or the equilibrium-driven depolymerization of poly(lactide). Any residual water which may be present in the polymer would also be removed during devolatilization, although it is recognized that a separate drying step may be utilized to reduce the water concentration to less than about 2,000 parts-per-million. The devolatilization of the lactide polymer may take place in any known devolatilization process. The key to selection of a process is operation at an elevated temperature and usually under conditions of vacuum to allow separation of the volatile components from the polymer. Such processes include a stirred tank devolatilization or a melt-extrusion process which includes a devolatilization chamber and the like. An inert gas sweep is useful for improved devolatization.

In a preferred process for manufacture of a melt-stable lactide polymer composition, the process also includes the step of adding a molecular weight control agent to the lactide prior to catalyzing the polymerization of the lactide. For example, molecular weight control agents include active hydrogen-bearing compounds, such as lactic acid, esters of lactic acid, alcohols, amines, glycols, diols and triols which function as chain-initiating agents. Such molecular weight control agents are added in sufficient quantity to control the number average molecular weight of the poly(lactide) to between about 10,000 and about 300,000.

Next referring to FIG. 1 which illustrates a preferred process for producing a melt-stable lactide polymer composition. A mixture of lactides enters a mixing vessel (3) through a pipeline (1). A catalyst for polymerizing lactide is also added through a pipeline (13). Within mixing vessel (3) a stabilizing agent may be added through a pipeline (2). A water scavenger may also be added through the pipeline (2). The stabilized lactide mixture is fed through a pipeline (4) to a polymerization process (5). The polymerized lactide or lactide polymer leaves the polymerization process through a pipeline (6). The stream is fed to a second mixing vessel (8) within which a stabilizing agent and/or catalyst deactivating agent may be added through a pipeline (7). The stabilized lactide polymer composition is then fed to a devolatilization process (10) through a pipeline (9). Volatile components leave the devolatilization process through a pipeline (11) and the devolatilized lactide polymer composition leaves the devolatilization process (10) in a pipeline (12). The devolatilized lactide composition is fed to a resin-finishing process (14). Within the resin-finishing process the polymer is solidified and processed to form a pelletized or granular resin or bead. Applicants recognize the polymer may be solidified and processed to form resin or bead first, followed by devolatilization. The resin is then fed to a drying process (16) by conveyance means (15). Within the drying process (16) moisture is removed as a vapor through pipeline (17). The dried lactide polymer resin leaves the drying process (16) by a conveyance means (18) and is fed to a melt-processing apparatus (19). Within the melt-processing apparatus (19) the resin is converted to a useful article as disclosed above. The useful article leaves the melt-processing apparatus (19) through a conveyance means (20).

The following examples further detail advantages of the system disclosed herein:

EXAMPLE 1

Polycaprolactone Blends

Polycaprolactone commercially available as TONE 787 from Union Carbide was added/mixed with poly(lactide) having a number average molecular weight of 157,900, a residual lactide concentration of 0.19%, a meso-lactide concentration of about 10% and a water concentration of less than about 500 ppm on a Leistritz twin screw extruder at 12.8%, 25.6%, 38.4% by weight to poly(lactide). These blends were injection molded into standard ASTM test bars using a Cincinnati Milacron Vista Sentry VST-55 molding press and physical properties were measured and tensiles tested on the bars. The above blends were also extruded into cast film on a Killion extruder with a sheet die, die gap 0.035", with 0.25% by weight Celite Super Floss diatomaceous earth for the purpose of an anti-block agent.

The following table illustrates critical data:

                  TABLE 1                                                          ______________________________________                                         Compounding: Twin Screw conditions                                                                 Cast Film: Killion Conditions                              ______________________________________                                         zone 1: 150° C.                                                                             zone 1: 286° F.                                     zones 2-8: 180° C.                                                                          zone 2: 320° F.                                     zones 9 % 10: 170° C.                                                                       zone 3: 320° F.                                     melt temp: 194° C.                                                                          zone 4: 315° F.                                     die pressure: 44 psi                                                                               adaptor: 310° F.                                    amps: 17.8-20.0     die temp: 310° F.                                   screw rpm: 300      pressure: 1340 psi                                         Pressure in                                                                    devolatization zone                                                            200 mm hg           screw rpm: 20.2                                            ______________________________________                                    

The following table illustrates the results. It is noted that blends of poly(caprolactone) and poly(lactide are more flexible than unblended poly(lactide) as shown by the increased elongation. This is significant for flexible films as well as other products where decreased brittleness is required.

                  TABLE 2                                                          ______________________________________                                                                              Break                                                                          Str. Modulus                              Film:    Mn:     Mw:     PDI: % Lactide                                                                             (kpsi)                                                                              (kpsi)                               ______________________________________                                         Sample 1 66662   157866  2.37 0.19   7.9  317                                  DVD 97                                                                         Sample 2 68364   170697  2.49 0.33   8.6  350                                  12.8% tone                                                                     Sample 3 95355   240973  2.53 0.08   N/A  N/A                                  25.6% tone                                                                     Sample 4 87013   221583  2.55 0.36   N/A  N/A                                  38.6% tone &                                                                   10% citro.A-4s                                                                 ______________________________________                                                       Break Str.                                                                               Modulus   Elongation                                   Injection Molded Test Bars:                                                                  (kpsi)    (kpsi)    at break (%)                                 ______________________________________                                         Sample 6 DVD-97                                                                              7.2       493       5.6 +- 1.9                                   Sample 7 12.7% tone                                                                          6.6       403       227 +- 52                                    Sample 8 25.6% tone                                                                          3.2       340       250 +- 133                                   Sample 9 38.6% tone                                                                          2.7       332       149 +- 58                                    ______________________________________                                    

EXAMPLE 2

Example Showing Orientation of Poly(lactide) for Film

To demonstrate the ease and benefit of making oriented poly(lactide) film, an experiment was done to make a sheet using poly(lactide) and orientating that sheet to different degrees. The polymer selected had a 280,000 to 400,000 weight average molecular weight, a 100,000 to 150,000 number average molecular weight, lactide concentration lower than 1%, meso level of about 10 to 20%, and a moisture level lower than about 500 ppm.

The sheet was cast using a 2" diameter single barrier flight screw Davis-Standard extruder with a 24:1 L/D. The die was 24" wide with an adjustable gap. The casting roll was 30" wide and 24" in diameter and equipped with temperature controls. After casting, the sheet was oriented in both the machine (MD) and transverse (TD) directions.

The MD orienter consisted of six 30" wide rolls and five temperature control zones: roll 1 and 2 were for preheat, roll 3 for slow draw, roll 4 for fast draw, roll 5 for heat setting, and roll 6 for cooling the sheet. Draw ratios up to 20 were used for the MD orientation.

The TD was a standard tenter frame with a 3 zone oven. The feed width range for the tenter was 8-48" and the output width range was 16-62". Following the orientation section was a slitter/winder.

Typical conditions used in extruding the sheet are shown below:

    ______________________________________                                         Extruder zone 1                                                                              350 to 400° F.                                                                      (177-204° C.)                                 zone 2        360 to 400° F.                                                                      (182-204° C.)                                 zone 3        340 to 350° F.                                                                      (171-188° C.)                                 Melt pip/adapters                                                                            330 to 350° F.                                                                      (166-177° C.)                                 Die zones     330° F.                                                   Head pressure 1640 to 2280 psi                                                 Screw speed   45 to 75 rpm                                                     ______________________________________                                    

Melt strength at the die was very good at 330° F. (166° C.). The die was positioned about 0.5 inch off the cast roll, which was run between 112° and 126° F. An air knife was used to pin the melt against the cast roll to reduce neck-in.

Conditions found useful for machine direction orientation of poly(lactide) were temperatures of 65° C. for the preheat rolls, 65° C. and 72° C. for the slow draw roll at low draw ratios and high draw ratios respectively, 65° C. for the fast draw roll, 45° C. for the heat roll, and 20° C. for the cooling roll.

The gap between the slow and fast roll was set to the minimum possible. Orientation took place only slightly above the Tg to give a high degree of molecular alignment. Rolls were collected after MD orientation and some were used for TD orientation.

Conditions for transverse direction orientation were 63° C. for the preheat zone, 70° C. for the stretching zone, and 6720 C for the annealing zone. Ambient air was circulated at the oven exit to cool the oriented sheet before winding.

The poly(lactide) oriented very well, being easily curved over the rolls and requiring lower process temperatures than standard plastic. The products made were:

    ______________________________________                                                MD        TD     Approx. Thickness                                      ______________________________________                                         Sample 1 0           0      5 mil                                              Sample 2 3.2         0      5 mil                                              Sample 3 3.5         4.3    1 mil                                              Sample 4 3.5         2.0    2 mil                                              Sample 5 1.5         2.9    9 mil                                              Sample 6 1.5         2.0    13 mil                                             ______________________________________                                    

Samples 1, 2 and 3 were tested for tensile and elongation according to ASTM D882 and tear resistance according to ASDTM D689. The results are shown below:

                  TABLE 3                                                          ______________________________________                                         Tensile Strength  Elongation Tear Strength                                     at break (lb/in/mil)                                                                             at break (%)                                                                              (g-cm)                                            ______________________________________                                         Sample 1                                                                               6.9           4.3        40                                                    7.4           4.8        40                                            Sample 2                                                                               15.8          85.1       16                                                    6.9           3.2        40                                            Sample 3                                                                               23.9          89.3       32                                                    10.5          160        128                                           ______________________________________                                    

As the data in the table shows, the tensile strength and flexibility of the poly(lactide) film can be greatly increased by orientation.

EXAMPLE 3

Non-Blocking Characteristics of Plasticized, Crystallized Poly(lactide)

Poly(lactide) having a weight average molecular weight of 165,000, a meso level of about 6%, a lactide level of less than about 0.2%, and a moisture level of less than about 500 ppm was blended with 25% by weight acetyl tributylcitrate (Citroflex A4 from Morflex) in a Werner & Pfleiderer twin screw extruder.

Two films of this composition were prepared in a Carver press equipped with heated platens at a temperature of 300°-350° F. and a dwell time of about 60 seconds. These films were annealed in an oven over four days to induce crystallization of the poly(lactide) samples. The films were tested for resistance to blocking at an elevated temperature. This test was performed by placing two films in contact with each other in an oven held at 60° C. with a 95 gram weight with a surface area of about 2.5 in² on top of the two films. After more than four hours, the films were removed from the oven and any adhesion between the films was noted. No adhesion occurred during the test. Prior to the annealing and crystallization procedure, films adhered to one another at room temperature.

This result shows that poly(lactide) films containing high levels of plasticizer will have adequate blocking resistance once the poly(lactide) is crystallized.

EXAMPLE 4

Anti-Block Aids

The use of anti-block aids can increase the resistance of two poly(lactide) films to stick together at elevated temperatures. This was demonstrated using poly(lactide) having a weight molecular weight of 165,000, a residual lactide level of about 0.1%, a meso level of about 10%, and a moisture level of about 60 ppm. The anti-block aid was diatomateous earth having a median particle size of 3.5 microns (Celite Super Floss from Celite) which was dried to a moisture level of about 400 ppm. The diatomaceous earth and poly(lactide) were blended in a twin screw extruder at different levels of anti-block aid and pelletized. The pellets were converted into film using the single screw extruder as in example 2. The films were tested for resistance to adhering to one another by placing two films together with a 92 gram weight on top in an oven set at 60° C. for 2 hours. A failure was when the films could not be separated after being removed from the oven. The results are shown in the table below:

                  TABLE 4                                                          ______________________________________                                                  % Celite                                                              Sample I.D.                                                                             Super Floss                                                                              Blocking Test 1                                                                             Blocking Test 2                                ______________________________________                                         2113-90-0                                                                               0.0       Fused        Fused                                          2113-90-1                                                                               4.1       None         None                                           2113-90-2                                                                               7.9       Some tiny pts. stuck                                                                        None                                           2113-90-3                                                                               1.8       Some pts. stuck                                                                             None                                           2113-90-4                                                                               0.9       Some pts. stuck                                                                             None                                           2113-90-5                                                                               0.45      Some pts. stuck                                                                             None                                           ______________________________________                                    

EXAMPLE 5

Anti-Blocking Agents

Two injection molded disks, 2.5 inch diameter, were placed together with a 94 gram weight on top and held at 50° C. for 24 hours. The disks had the following agents compounded therein. The disks were then cooled to room temperature and pulled apart by hand and ranked for blocking characteristics (considerable, slight and none). The following are the results:

                  TABLE 5                                                          ______________________________________                                         AGENTS                                                                         ______________________________________                                         Poly(lactide) control considerable                                             22% wheat gluten      none                                                     10% wheat gluten      slight                                                   22% pecan shell       none                                                     15% pecan shell       slight                                                   23% wollastonite      slight                                                   28% Ultratalc 609     none                                                     23% Ultratalc 609     none                                                     28% Microtuff F talc  slight                                                   22% Microtuff F talc  slight                                                   14% Microtuff F talc  slight                                                    2% Microtuff F talc  considerable                                             ______________________________________                                    

EXAMPLE 6

Plasticizer Agents

Dried pellets of devolatilized poly(lactide) were processed in a twin screw extruder to allow compounding of various plasticizing agents. The strands leaving the extruder were cooled in a water trough and chopped into pellets. Samples of the pellets were heated at 20° C./minute to 200° C. in a DSC apparatus, held at 200° C. for 2 minutes and rapidly cooled to quench the samples. The quenched samples were then reheated in the DSC apparatus increasing at 20° C./minute to determine the glass transition temperature. These samples were compared to a polymer with no plasticizer. The effect of the plasticizer on the glass transition temperature is shown in the table below. Glass transition temperatures are taken at the mid-point of the transition.

                  TABLE 6                                                          ______________________________________                                                                 Change in T.sub.g /wt.                                 SAMPLE           T.sub.g (C)                                                                           percent additive                                       ______________________________________                                         Control          54.8   --                                                     8% Dioctyl adipate                                                                              35.0   2.5                                                    Control + 40% silica                                                                            54.5   --                                                     Control + 40% silica +                                                                          36.0   3.7                                                    5% dioctyl adipate                                                             Control          54.6   --                                                     6% Citroflex A-4*                                                                               42.6   2.0                                                    12% Citroflex A-4                                                                               31.4   1.9                                                    Control          59.3   --                                                     1.6% Citroflex A-4                                                                              56.3   1.9                                                    2.9% Citroflex A-4                                                                              53.1   2.1                                                    Control          58.4   --                                                     2.1% Citroflex A-4                                                                              56.1   1.1                                                    3.4% Citroflex A-4                                                                              50.5   2.3                                                    Control          61.6   --                                                     18.6% Citroflex A-2                                                                             54.7   0.4                                                    13.1% Citroflex B-6                                                                             52.4   0.7                                                    12.6% Citroflex A-6                                                                             53.8   0.6                                                    ______________________________________                                          *Citroflex is a registered trademark of Morflex, Inc., Greensboro, NC. A4      is the designation of a purified acetyltrin-butyl citrate. A2 is the           designation of acetyltriethyl citrate, A6 is the designation of                acetyltrin-hexyl citrate, and B6 is the designation of nbutyryltri-n-hexy      citrate.                                                                 

These results show the effectiveness of these plasticizers in reducing the glass transition temperature of poly(lactide).

The procedure above was tried using corn oil as a plasticizer. Visual observation showed the corn oil to be not compatible, forming a film on the surface. Corn oil and mineral oil were both not effective as a primary plasticizer with poly(lactide). They may still be useful as a secondary plasticizer, in combination with a compatible primary plasticizer.

EXAMPLE 7

Lactide and Poly(lactide) Equilibrium Concentrations

Experiments were conducted to determine the equilibrium concentration of lactide and poly(lactide) at different temperatures. In these experiments a sample of lactide was polymerized in the presence of a catalyst (tin (II) bis-(2-ethyl hexanoate)) and held at a fixed temperature for 18 hours or greater. Beyond this time the residual monomer concentration is believed essentially constant. The content of residual monomer was determined by GPC analysis. GPC analysis was conducted with an Ultrastyragel® column from Waters Chromatography. The mobile phase was chloroform. A refractive index detector with molecular weight calibration using polystyrene standards was used. The GPC temperature was 35° C. Data analysis was completed using the software package Baseline, model 810, version 3.31.

The results of tests conducted on several samples at various temperatures are summarized in the graph of FIG. 2 as indicated by X's on such graph. Also plotted on the graph of FIG. 2 are data points cited in A. Duda and S. Penczek, Macromolecules, vol. 23, pp. 1636-1639 (1990) as indicated by circles on the graph. As can be seen from the graph of FIG. 2, the equilibrium concentration, and thus the driving force behind the depolymerization of poly(lactide) to form lactide, increases dramatically with increased temperature. Thus, melt-processing at elevated temperatures results in degradation of the lactide polymer to form lactide on the basis of equilibrium alone. For example, lactide concentrations below about 2 percent cannot be directly obtained at temperatures of 140° C. or above due to the identified equilibrium relationship between lactide and poly(lactide).

EXAMPLE 8

Lactide Polymerization in the Presence of a Solid Supported Catalyst

Tin (II) Oxide

24 grams of L-lactide (melting point about 97° C.) and 6 grams of D,L-lactide (for the purposes of this invention, D,L-lactide has a melting point of about 126° C.) were combined in a round bottom flask with 0.033 grams of Tin (II) oxide, as a fine powder. This corresponds to the catalyst level of 852:1, molar ratio lactide to tin. The flask was then purged with dry nitrogen 5 times. This was lowered into an oil bath at 160° C. with magnetic stirring. Polymerization time was 8 hours.

Amberlyst 36

24 grams of L-lactide and 6 grams of D,L-lactide were combined in a round bottom flask with 1.06 grams of Amberlyst 36 resin beads. The flask was purged 5 times with dry nitrogen. The flask was lowered into an oil bath at 140° C. with magnetic stirring. Polymerization time was 8 hours. The resin had a stated proton content of 1 meq/gram dry weight resin. The resin was prepared by rinsing 2 times with 10 volumes dry methanol, then dried for several hours under high vacuum for several hours at 40° C.

The polymerization results are shown below:

                  TABLE 7                                                          ______________________________________                                         Sample     Mn      Mw        PDI  % Conversion                                 ______________________________________                                         Tin (II) Oxide                                                                            77,228  103,161   1.34 54.0                                         Amberlyst   1,112   1,498    1.34 73.5                                         ______________________________________                                    

Molecular Weight Relationship to Physical Properties of Lactide Polymers

Poly(lactide) samples with various molecular weights and optical compositions were prepared by polymerizing blends of L-lactide and meso-lactide at 180° C. under nitrogen in a 1-gallon sealed reactor. Tin(II) bis(2-ethyl hexanoate) catalyst was added at a monomer-to-catalyst ratio of 10,000:1. After about 1 hour the molten polymer was drained from the reactor using nitrogen pressure. The sample was poured into a pan and placed in a vacuum oven at about 160° C. for about 4 hours to bring the reaction to near equilibrium levels.

Portions of the samples were then dried under vacuum and processed in an injection molding apparatus (New Britain 75 from New Britain Machine Co.) to produce standard test bars for physical property testing. The results of physical property testing are shown in the following Table 8. The physical property tests were made according to ASTM methods D 638, D 256, and D 790. The reported results are the averages of several tests.

Samples of the test bars after injection molding were analyzed by GPC for molecular weight. Other portions of the test bars were reground and tested in a capillary viscometer to determine the melt-viscosity. These results are also included in Table 8.

Statistical analysis of the data revealed no correlations which were statistically significant between either optical composition or molecular weight and the mechanical properties of modulus, tensile strength, percentage elongation at break, notched Izod impact strength, flexural modulus, or flexural strength. The independence of these properties on molecular weight indicates that all of these samples were above a "threshold" molecular weight required to achieve the intrinsic properties of the polymer in a preferred composition.

The viscosity data show significant correlations with molecular weight. This dependence documents the practical limitation and necessity of controlling polymer molecular weight below an upper limit at which it is impractical to melt-process the polymer. At high molecular weight, high viscosity prevents processing by standard melt-processing equipment. Increases in temperature to reduce viscosity dramatically increase polymer degradation and lactide formation which is also unacceptable.

                                      TABLE 8                                      __________________________________________________________________________                   Molecular                                                                      Weight After                                                                         Viscosity at 173° C. (Pa · S)              Sample                                                                             Meso Lactide                                                                             Injection                                                                            Final  Shear Rate                                                                          Shear Rate                                     I.D.                                                                               In Blend, Wt %                                                                           Weight                                                                               IV (dl/g)                                                                             100 S.sup.-1                                                                        1000 S.sup.-1                                  __________________________________________________________________________     6   40        41000 0.86    5.5 2.9                                            5   10        54000 0.88   10.4 7.2                                            4   20        59000 0.91   10.4 7.2                                            8   10        64000 1.02   15.7 10.0                                           9   40        68000 0.97   12.6 8.1                                            7   20        71000 1.16   36.0 12.9                                           10  20        83000 1.19   35.8 15.8                                           __________________________________________________________________________     Mechanical Properties of Injection Molded Samples                                        Tensile            Flexural                                                                             Flexural                                    Sample                                                                              Modulus                                                                             Strength                                                                            % Elongation                                                                          IZOD Impact                                                                           Modulus                                                                              Strength                                    I.D. MPSI (Yld) PSI                                                                           at Break                                                                              ft · lb./in                                                                  MPSI  PSI                                         __________________________________________________________________________     6    0.55 6600 3.3    0.39   0.53  11300                                       5    0.56 7800 3.5    0.46   0.54  12500                                       4    0.56 7600 3.9    0.32   0.53  12500                                       8    0.55 7700 3.4    0.47   0.53  12400                                       9    0.59 6700 3.1    0.42   0.52  10600                                       7    0.56 7400 3.3    0.45   0.51  12400                                       10   0.55 6700 3.0    0.47   0.52   9900                                       __________________________________________________________________________

EXAMPLE 10

Effect of Residual Catalyst on Polymer Degradation

Polymer samples were prepared at four levels of catalyst, corresponding to monomer to catalyst molar ratios of 5,000:1, 10,000:1, 20,000:1, and 40,000:1. The catalyst utilized was tin (II) bis(2-ethyl hexanoate). These samples were then subjected to heating in a TGA apparatus (TA Instruments, Inc., model 951 thermogravometric analyzer with a DuPont 9900 computer support system) with a nitrogen purge. Isothermal conditions of 200° C. for 20 minutes were used. The samples were then analyzed by GPC with a viscosity-based detector and a universal calibration curve to determine the extent of breakdown in molecular weight. The GPC apparatus for this test was a Viscotek Model 200 GPC and a Phenomenex column. The TGA analysis typically resulted in about a 5 percent loss in weight and molecular weight drops of 0 to 70 percent.

The number average molecular weights were converted to a milliequivalent per kilogram basis (1,000,000/Mn) in order to calculate a rate of chain scission events. The results below represent averages of 2-4 replicates on each of the four samples.

                  TABLE 9                                                          ______________________________________                                         Catalyst level  Scission Rate                                                  (monomer/catalyst)                                                                             (meq/kg*min)                                                   ______________________________________                                          5,000          1.33                                                           10,000          0.62                                                           20,000          0.44                                                           40,000          0.12                                                           ______________________________________                                    

The rate of chain scission was directly proportional to the residual catalyst level, demonstrating the detrimental effect of catalyst activity on melt-stability under conditions similar to melt-processing. This instability, however, is distinguished from the instability due to the equilibrium relationship between lactide and poly(lactide) detailed in Example 7, in that loss of molecular weight due to catalytic depolymerization by chain scission is evident.

EXAMPLE 11

Catalyst Deactivation Experiment

Two runs were made in a laboratory Parr reactor. Lactide feed was 80 percent L-lactide and 20 percent D,L-lactide. Molecular weight was controlled by adding a small quantity of lactic acid, the target molecular weight was 80,000 Mn.

Lactide was charged to the reactor as a dry mix, the reactor was purged 5 times with nitrogen, and heated up to 180° C. At this point catalyst (5000:1 initial monomer to catalyst molar ratio, Fascat® 2003) was charged through a port in the top of the reactor. The reaction was allowed to proceed for 70 minutes at 180° C., with mechanical agitation. Conversion at this point was 93-94 percent, close to the equilibrium value at 180° C. of 96 percent poly(lactide) from FIG. 2. This point is considered t-zero, designating the completion of the polymerization reaction and the beginning of the mixing time.

In the control experiment, a sample was taken and the mixture was held at temperature with continued agitation. Samples were taken periodically through a port in the reactor bottom. After 4 hours the reactor was drained.

In the example experiment, a sample was taken and 0.25 weight percent of a metal deactivator (Irganox® MD 1024®) was added through the catalyst addition port. The mixture was held at temperature with continued agitation and samples were withdrawn periodically. The reactor was drained after 4 hours.

GPC analysis (utilizing the method of Example 7) for these samples was divided into three parts: polymer with molecular weight over 4,000 (for which the Mn and Mw numbers are reported), the percent oligomers (comprising the region with molecular weight greater than lactide but less than 4,000, as distinguished from oligomers as defined by Loomis to include only oligomers up to a molecular weight of 450), and percent lactide (residual monomer). The structure of the oligomers was not certain, but it is believed they were primarily cyclic structures. It is also believed that the metal deactivator, if unreacted, will elute with the oligomer fraction. Quantification of the oligomer fraction is difficult, because the GPC trace is near the baseline in this region.

The analysis of the polymer samples as withdrawn from the reactor at various time intervals for the control and experimental compositions are shown below in Table 10.

                  TABLE 10                                                         ______________________________________                                         Control                                                                              Mn      Mw       % Polymer                                                                              % Oligomer                                                                             % Monomer                               ______________________________________                                         t-zero                                                                               67,100  119,500  94      0       6.0                                     0.5 hr                                                                               62,500  119,000  95      0.7     3.9                                     1.0 hr                                                                               61,500  116,100  96      0       3.6                                     1.5 hr                                                                               56,000  111,600  95      1.5     3.3                                     2.0 hr                                                                               57,600  110,900  96      0.9     3.1                                     4.0 hr                                                                               51,400  105,400  94      3.3     3.1                                     ______________________________________                                         Test  Mn      Mw       % Polymer                                                                              % Oligomer                                                                             % Monomer                               ______________________________________                                         t-zero                                                                               63,200  110,700  93      3.5     3.8                                     0.5 hr                                                                               52,100  108,600  92      4.6     2.9                                     1.0 hr                                                                               52,700  109,200  92      4.9     2.8                                     1.5 hr                                                                               53,400  107,200  93      4.0     3.1                                     2.0 hr                                                                               59,700  111,100  94      0.6     5.8                                     4.0 hr                                                                               51,200  107,300  91      6.1     3.3                                     ______________________________________                                    

The samples were then ground and placed in a 120° C. oven under vacuum (pressure 0.1 inch Hg) for 14 hours. Sample analyses after this treatment are shown below in Table 11.

                  TABLE 11                                                         ______________________________________                                         Control                                                                              Mn      Mw       % Polymer                                                                              % Oligomer                                                                             % Monomer                               ______________________________________                                         t-zero                                                                               45,500  88,500   98      2.2     0.0                                     0.5 hr                                                                               45,000  88,700   98      2.0     0.0                                     1.0 hr                                                                               43,900  87,200   98      2.0     0.0                                     1.5 hr                                                                               42,600  84,000   98      2.2     0.0                                     2.0 hr                                                                               42,000  85,200   97      3.2     0.0                                     4.0 hr                                                                               41,900  82,800   98      2.0     0.0                                     ______________________________________                                         Test  Mn      Mw       % Polymer                                                                              % Oligomer                                                                             % Monomer                               ______________________________________                                         t-zero                                                                               39,300  76,700   96      4.0     0.0                                     0.5 hr                                                                               43,900  85,100   98      2.4     0.0                                     1.0 hr                                                                               55,300  98,600   96      3.8     0.0                                     1.5 hr                                                                               48,400  96,200   95      4.5     0.0                                     2.0 hr                                                                               48,900  101,900  95      5.0     0.0                                     4.0   50,600  101,900  94      5.6     0.0                                     ______________________________________                                    

In all cases the polymer was completely devolatilized (0.0 percent residual lactide monomer). The data also clearly show that the metal deactivator reduced the degradation of polymer during the devolatilization step (as indicated by the greater loss in Mn for the control samples from Table 9 to Table 10 versus the Test samples). One hour of mixing appears to be long enough to develop most of the benefit.

The samples were stored at room temperature under nitrogen for about 1 week and reanalyzed, as shown below in Table 12.

                  TABLE 12                                                         ______________________________________                                         Control                                                                              Mn      Mw       % Polymer                                                                              % Oligomer                                                                             % Monomer                               ______________________________________                                         t-zero                                                                               33,500  71,000   100     0.1     0.0                                     0.5 hr                                                                               43,400  95,800   99      1.0     0.0                                     1.0 hr                                                                               44,900  96,300   100     0.1     0.0                                     1.5 hr                                                                               45,900  95,000   100     0.0     0.0                                     2.0 hr                                                                               45,900  94,100   100     0.2     0.0                                     4.0 hr                                                                               43,100  90,100   99      1.3     0.0                                     ______________________________________                                         Test  Mn      Mw       % Polymer                                                                              % Oligomer                                                                             % Monomer                               ______________________________________                                         t-zero                                                                               44,600  84,900   100     0.0     0.0                                     0.5 hr                                                                               45,300  90,600   99      1.2     0.0                                     1.0 hr                                                                               47,800  100,000  98      2.4     0.0                                     1.5 hr                                                                               46,600  98,900   96      3.5     0.0                                     4.0   57,700  110,200  96      4.0     0.3                                     ______________________________________                                    

Equilibrium lactide levels are estimated to be less than 0.2 weight percent at room temperature. Consistent with that, essentially no lactide was observed in any of the samples (detection limit about 0.1 weight percent). The oligomer content in the non-stabilized samples declined and some increase in molecular weight was noted, perhaps due to reincorporation of the (cyclic) oligomers into the polymer. The oligomer depletion reaction was inhibited in the stabilized polymers, with the extent of inhibition dependent on the length of time that the additive was mixed.

The samples were then reheated to 180° C. in sealed vials and held for one hour as a simulation of melt-processing. Analysis of the samples after the heat treatment is given below in Table 13.

                  TABLE 13                                                         ______________________________________                                         Mn        Mw       % Polymer % Oligomer                                                                             % Monomer                                 ______________________________________                                         Control                                                                        t-zero                                                                               23,900  60,000   88      8.4     4.0                                     0.5 hr                                                                               23,900  59,600   90      7.7     2.7                                     1.0 hr                                                                               23,700  58,800   88      9.3     2.7                                     1.5 hr                                                                               24,700  58,000   86      10.0    3.8                                     2.0 hr                                                                               26,100  56,400   90      6.8     2.7                                     4.0 hr                                                                               24,800  58,700   92      6.6     1.9                                     Test                                                                           t-zero                                                                               33,900  64,300   95      2.2     3.1                                     0.5 hr                                                                               17,900  34,600   94      4.8     1.7                                     1.0 hr                                                                               21,200  42,900   94      4.6     1.8                                     1.5 hr                                                                               29,200  56,900   98      0.5     1.8                                     2.0 hr                                                                               missing                                                                  4.0 hr                                                                               35,700  71,400   95      3.7     1.7                                     ______________________________________                                    

The data for molecular weight show that if the metal deactivator is not mixed into the system long enough then it can have a detrimental impact on stability in the melt. The samples for which the mixing was at least 1.5 hours show no detrimental effect, and the 4 hour sample appears to be somewhat more stable than any of the others based on molecular weight alone. More importantly, the metal deactivator samples show significantly less lactide reformation than the control samples. This effect is gained even in the samples which were mixed for only 0.5 hour. The metals deactivated samples averaged only 1.8 percent lactide after one hour at 180° C., compared to an average of 3.0 percent lactide for the controls. The equilibrium level at 180° C. is about 3.6 percent from FIG. 2. Thus, the use of metal deactivators can reduce the troublesome reformation of lactide during melt-processing of the finished polymer.

EXAMPLE 12

Effect of Increased Polymerization Temperature on Polymer Characteristics

L-lactide (Boeringer Ingleheim, S-grade) was used as received, meso-lactide (PURAC) was purified by distillation to remove traces of D- and L-lactide. The melting point of the purified meso-lactide was 54° C. Lactide mixtures were made up to the following ratios: 100 percent L-lactide, 90/10 L-lactide/meso-lactide, 70/30 L-lactide/meso-lactide, 50/50 L-lactide/meso-lactide, and 100 percent meso-lactide. Catalyst level was 2,500:1 molar ratio of initial monomer to tin with the tin being tin(II) bis (2-ethyl hexanoate) (Fascat® 9002). Lactic acid was added as a molecular weight control agent to target a number average molecular weight of 50,000 (the same amount was added to all samples). Polymerization times were estimated to obtain conversions of 50 percent and 90 percent. For 120° C. this was 4 hours and 16 hours, respectively. For 180° C. these times were 10 minutes and 50 minutes, respectively. Below in Table 14 are the GPC results (method of Example 7) of tests on the polymer samples produced by this procedure.

                  TABLE 14                                                         ______________________________________                                         L/meso   Temp     Mn       Mw     PDI   % Conv                                 ______________________________________                                         100% L   120° C.                                                                          31,014   33,774 1.09  53.2                                                     45,864   52,574 1.15  87.1                                   100% L   180° C.                                                                          27,785   32,432 1.17  46.7                                                     56,839   98,125 1.73  93.3                                   90/10    120° C.                                                                          34,541   38,586 1.12  62.3                                                     29,222   34,466 1.18  89.3                                   90/10    180° C.                                                                          31,632   35,713 1.13  48.5                                                     57,925   110,841                                                                               1.91  94.8                                   70/30    120° C.                                                                          41,211   45,222 1.10  60.1                                                     58,284   71,257 1.22  89.1                                   70/30    180° C.                                                                          32,292   37,401 1.16  53.8                                                     51,245   107,698                                                                               2.10  96.5                                   50/50    120° C.                                                                          15,888   17,969 1.13  57.8                                                     25,539   31,834 1.25  90.6                                   50/50    180° C.                                                                          34,375   42,018 1.22  62.5                                                     44,590   98,028 2.20  95.5                                   100% meso                                                                               120° C.                                                                          33,571   40,635 1.21  73.4                                                     45,237   68,142 1.51  94.3                                   100% meso                                                                               180° C.                                                                          30,976   42,987 1.39  67.6                                                     40,038   83,815 2.09  96.6                                   ______________________________________                                    

The results show that the ultimate number average molecular weight was not significantly affected by the temperature of polymerization, with an average of 41,000 at 120° C. and 50,000 at 180° C. This implies that each lactic acid molecule initiates about one polymer chain, regardless of temperature. The ultimate weight average molecular weight is, however, significantly affected by temperature. At 120° C. the weight average molecular weight averaged 52,000 and at 180° C. the average was 100,000. This is believed to be due to a relative increase in the rate of transesterification at 180° C. The polydispersity index (PDI) at high conversion also reflects this, averaging 1.3 at 120° C. and 2.0 at 180° C. It is believed these differences would have a significant effect on the melt-processing characteristics of the polymer, with the higher weight average molecular weight of the polymer produced at 180° C. expected to translate into better melt strength and processability.

These experiments show that polymerization at a higher temperature results in a polymer that is characteristically different. Further, the glass transition temperature for the samples polymerized at higher temperature is higher.

EXAMPLE 13

Experiments with Stabilizing Agents and Metal Deactivators

Test 1

Conditions: vial polymerization, (Lactide is melted under a nitrogen-purged atmosphere in a round bottom flask with stirring. Catalyst and additives are added and aliquots of the mixtures are pipetted into silanized glass vials. Typically 5-10 grams of reaction mixture are used in a 16 ml. vial. The vials are tightly capped and placed into a preheated oil bath.) 10,000:1 molar ratio of lactide-to-tin, tin(II) bis(2-ethyl hexanoate) catalyst, 0.2 wt percent Ultranox®626 in tetrahydrofuran (THF). 180° C. Time was 90 minutes.

The control with tin only polymerized to 84 percent conversion and reached a MWn of 31,700. The example with tin and Ultranox® polymerized to 83 percent conversion and reached a number average molecular weight (MWn) of 39,800; an increase of 26 percent over the control.

The control sample turned light yellow, the sample with stabilizer remained colorless.

Test 2

Conditions: vial polymerization, 5000:1 molar ratio of lactide to tin, tin(II) bis(2-ethyl hexanoate) catalyst, 0.25 wt percent Ultranox®626 (in THF). 180° C. Time was 60 minutes. Lactide was used from the above described Gruber et al. process.

The control with tin alone polymerized to 67 percent conversion and reached a MWn of 62,900. The example with tin and Ultranox® polymerized to 66 percent conversion and reached a MWn of 75800; an increase of 21 percent over the control.

A second example with tin(II) bis(2-ethyl hexanoate), Ultranox®, and 0.50 percent of Irganox® 1076, which is a phenolic antioxidant, polymerized to 66 percent conversion and reached a number average molecular weight (MWn) of 74500; an increase of 18 percent over the control.

All samples were a dark yellow color, although the samples with stabilizer had a slightly lower absorbance at 300 nm.

Test 3

Conditions: vial polymerization, 10,000:1 molar ratio of lactide to tin, tin(II) bis(2-ethyl hexanoate) catalyst, 180° C., 80 percent L-lactide and 20 percent D,L-lactide purchased from Henley and Aldrich, respectively. Lactic acid was added to control molecular weight to about 75,000 at full conversion. One sample included 0.25 percent Ultranox® 626 phosphite stabilizer, one included 0.25 percent Irganox® 1076 antioxidant, and one control sample.

Samples were taken at various times and analyzed by GPC for conversion and molecular weight (the method of Example 7). The results are summarized in Table 9 below.

                  TABLE 15                                                         ______________________________________                                         Time Control      Irganox ®                                                                               Ultranox ®                                  (hrs)                                                                               Mn       % conv  Mn     % conv                                                                               Mn      % conv                              ______________________________________                                         1    31,000   46      35,900 41    66,500  61                                  2    45,400   74      56,800 74    102,700 83                                  4    69,600   93      74,100 93    97,200  91                                  11   52,900   95      60,700 95    71,500  94                                  ______________________________________                                    

The sample with phosphite stabilizer polymerized faster, shown by the higher conversion at 1 and 2 hours, and went to a higher molecular weight than the control or the sample with Irganox®. The phosphite stabilized sample had a molecular weight more than 30 percent higher than the control for all time periods.

Test 4

The experiment above was repeated to compare the control to the phosphite-stabilized polymer, as summarized in Table 16 below.

                  TABLE 16                                                         ______________________________________                                         Time     Control            Ultranox ®                                     (hrs)    Mn      % conv     Mn     % conv                                      ______________________________________                                         1        36,600  37         71,500 59                                          2        51,700  70         95,200 85                                          4        64,400  91         103,700                                                                               94                                          8        58,100  96         95,700 94                                          ______________________________________                                    

The sample with phosphite stabilizer again polymerized faster and went to a higher molecular weight than the non-stabilized sample. The phosphite stabilized sample had a molecular weight more than 60% higher than the control for all time periods.

Test 5

Conditions: vial polymerization, 5,000:1 molar ratio of lactide to tin, tin(II) bis(2-ethyl hexanoate) catalyst, 180° C., 80 percent L-lactide and 20 percent D,L-lactide purchased from Henley and Aldrich. Lactic acid was added to control number average molecular weight to an estimated 80,000 at full conversion. One sample was run with 0.25 percent Ultranox® 626 phosphite stabilizer, one with 0.25 percent Irganox® 1076 antioxidant, and one control sample.

Samples taken at various times and analyzed by GPC (the method of Example 1) for conversion and molecular weight. The results are tabulated in Table 17 below.

                  TABLE 17                                                         ______________________________________                                         Time Control      Irganox ®                                                                               Ultranox ®                                  (hrs)                                                                               Mn      % conv   Mn     % conv                                                                               Mn      % conv                              ______________________________________                                         1    83,600  76       121,900                                                                               83    162,300 87                                  4    74,400  93       104,300                                                                               95    123,900 96                                  24   40,200  96       52,000 96    96,900  97                                  48   34,200  97       30,400 96    56,500  96                                  72   25,000  96       22,400 96    69,500  96                                  ______________________________________                                    

The phosphite-stabilized sample had a molecular weight more than 60 percent higher than the control for all time periods. After 72 hours it had a molecular weight 2.8 times higher than the control. The sample with antioxidant showed an initial increase in molecular weight, relative to the control, but the effect disappeared after 48 hours.

The phosphite stabilized sample was significantly lighter in color than the control or the antioxidant treated sample.

Test 6

Conditions: vial polymerization, 5000:1 molar ratio of lactide to tin, tin(II) bis(2-ethyl hexanoate) catalyst, 0.25 wt percent Ultranox®626 (in THF). 180° C. Time was two hours. Gruber et al. process lactide washed with isopropyl alcohol was used.

The control with tin alone polymerized to 95 percent conversion and reached a number average molecular weight of 118,000. The example with tin and Ultranox® polymerized to 93 percent conversion and reached a number average molecular weight of 151,000, an increase of 28 percent over the control.

Test 7

Conditions: vial polymerization at 180° C. 5000:1 molar ratio of lactide to tin, tin(II) bis(2-ethyl hexanoate) catalyst. Lactide was 80 percent L-lactide and 20 percent D,L-lactide, purchased from Henley and from Aldrich. Lactic acid was added to target the molecular weight to an Mn of 80,000. All stabilizers were added at 0.25 weight percent. Molecular weight (number average) was determined for samples pulled at 3 hours, while rate constants were based on samples pulled at 1 hour. The results of these screening tests on many stabilizing agents following the above procedure are detailed below in Table 18. Product designations in Table 18 are tradenames or registered trademarks.

                  TABLE 18                                                         ______________________________________                                                                              Relative                                  Sample           MWn      % Conversion                                                                              Rate                                      ______________________________________                                         Control 1            65,000   95.9     90                                      Control 2            85,000   95.9     100                                     Control 3            76,000   96.6     100                                     Control 4            69,000   96.2     100                                     Control 5            74,000   96.8     110                                     Control 6            70,000   97.2     110                                     PHOSPHITES                                                                     Ultranox 626                                                                              (GE)      103,000  96.8     100                                     Weston TDP (GE)      64,000   70.0     60                                      Weston PDDP                                                                               (GE)      67,000   76.7     60                                      Weston PNPG                                                                               (GE)      92,000   94.1     100                                     Irgafos 168                                                                               (Ciba-Geigy)                                                                             95,000   95.3     120                                     Weston 618 (GE)      99,000   95.1     100                                     Sandostab P-EPQ                                                                           (Sandoz)  108,000  94.7     110                                     Weston TNPP                                                                               (GE)      88,000   97.9     130                                     PHENOLIC                                                                       ANTIOXIDANTS                                                                   Irganox 1010                                                                              (Ciba-Geigy)                                                                             95,000   97.5     110                                     Cyanox 1790                                                                               (Cyanamid)                                                                               98,000   96.9     120                                     BHT                  87,000   96.5     130                                     Irganox 1076                                                                              (Ciba-Geigy)                                                                             121,000  97.8     130                                     Topanol CA (ICI)     84,000   96.6     160                                     AMINES                                                                         Tinuvin 123                                                                               (Ciba-Geigy)                                                                             65,000   94.8     70                                      Tinuvin 622                                                                               (Ciba-Geigy)                                                                             82,000   95.7     80                                      Naugard 445                                                                               (Uniroyal)                                                                               93,000   98.2     120                                     THIOETHER                                                                      Mark 2140  (Witco)   77,000   97.0     120                                     METAL                                                                          DEACTIVATORS                                                                   Irganox MD1024                                                                            (Ciba-Geigy)                                                                             34,000   65.7     10                                      Naugard XL-1                                                                              (Uniroyal)                                                                               91,000   95.8     110                                     ______________________________________                                    

Note, that with a few exceptions, the phosphites and the phenolic antioxidants provide increased molecular weight with no reduction in polymerization rate. Of the amines, only Naugard® 445 provided stabilization without a rate decrease. The metal deactivators are expected to deactivate the catalyst, as was observed for Irgnaox® MD1024. The Naugard® XL-1 did not accomplish deactivation.

EXAMPLE 14

Polymer Melt Stability as a Function of Moisture Content

Lactide, produced and purified in a continuous (Gruber et al.) process, was fed at a rate of 3 kg/hr to a continuous polymerization pilot plant. Catalyst was added with a metering pump at the rate of 1 part catalyst to 5000 parts lactide on a molar basis. The reaction system was blanketed with nitrogen. The reactor vessels consist of two continuous stirred tank reactors (CSTR) in series. The first had a 1-gallon capacity and the second had a 5-gallon capacity. The reactors were run 60-80 percent liquid filled and at 170°-180° C. Polymer melt pumps moved the liquid from CSTR 1 to CSTR 2, and from CSTR 2 through a die into a cooling water trough. The polymer strand thus produced was pulled from the trough by a pelletizer and stored as pellets.

The pelletized poly(lactide) was put into a drying hopper and dried at 40° C. under flowing dry air. Samples were pulled after one hour and four hours. These samples were then run through a single screw Brabender® extruder, with a retention time of approximately 3 minutes. Samples were analyzed for moisture by an automatic Karl Fischer apparatus and for molecular weight by GPC (the method of Example 7). The results of these tests are documented in Table 19 below.

                  TABLE 19                                                         ______________________________________                                                      Extruder    Weight Average                                        Sample       Temperature (C.)                                                                           Molecular Weight                                      ______________________________________                                         Initial                  63,000                                                Dried 1 hour 137         44,000                                                (1200 ppm H.sub.2 O)                                                                        145         48,000                                                             162         35,000                                                             179         30,000                                                Dried 4 hours                                                                               140         63,000                                                (150 ppm H.sub.2 O)                                                                         140         69,000                                                             160         65,000                                                             178         68,000                                                ______________________________________                                    

These results show the detrimental effect of water in the lactide polymer resin during melt polymerization and the need to properly dry the poly(lactide) before melt-processing.

EXAMPLE 15

Degradation of Crystalline and Amorphous Poly(lactide)

Two literature references disclose poly(D,L- lactide) to degrade faster than poly(L-lactide), attributing the result to crystallinity of poly(L-lactide). These are: Kulkarni et al., J. Biomed. Mater. Res., vol. 5, pp. 169-181, (1971); Makino et al., Chem. Pharm. Bull., vol. 33, pp. 1195-1201, (1985). An experiment was conducted to measure the effect of crystallinity on polymer degradation and is detailed below.

An amorphous poly(lactide) sample (clear, and less than 1 percent crystallinity based on DSC) and a crystalline poly(lactide) sample (opaque, and approximately 50 percent crystallinity based on DSC) were subjected to biodegradation in a compost test (50° C., with aeration). The DSC apparatus was a TA Instruments, Inc., model 910 differential scanning calorimeter with DuPont 9900 computer support system typically programmed to heating at a rate of 10° C. per minute to 200° C. The samples had different optical composition, with the crystalline sample being more than 90 percent poly(L-lactide) and the amorphous sample being less than 80 percent poly(L-lactide) with the balance being either poly(D,L-lactide) or poly(meso-lactide). Samples of each polymer were subjected to a compost test (ASTM D 5338) which included mixing a stabilized compost and providing a source of humidified air while maintaining a temperature of about 50° C. The amorphous sample was completely degraded after 30 days of composting. The crystalline sample was only 23 percent degraded based on carbon dioxide after the same period of time.

Additional samples of these two polymers were subjected to chemical hydrolysis at 50° C. (hydrolysis is believed to be the rate-limiting step in the biodegradation process). The chemical hydrolysis procedure included placing 0.1 gram poly(lactide) in 100 ml of 0.2M phosphate buffer (pH=7.4). The samples were held for 1 week, then filtered, washed with deionized water, and dried at 25° C. under vacuum. The initial weight average molecular weight for each sample was about 70,000. After 1 week the amorphous sample had a weight average molecular weight of 10,000 and the crystalline sample had a weight average molecular weight of 45,000, determined by GPC (the method of Example 7). Neither sample had significant weight loss at this time.

Both of these tests demonstrate that degradation of crystalline poly(lactide) is slower than degradation of amorphous poly(lactide).

EXAMPLE 16

Effect of Monomer Concentration on Film Modulus

Poly(lactide) was precipitated in methanol from a chloroform solution in order to remove the residual lactide monomer. GPC analysis (the method of Example 1) showed the precipitated polymer to contain 0.0 percent lactide.

The polymer was dissolved in chloroform to make a 10 wt percent solution, and lactide was added back to make 5 separate solutions which, after removing the chloroform, are calculated to produce films containing 0.0, 0.2, 0.4, 1.0 and 4.0 weight percent lactide in poly(lactide). These solutions were solvent cast onto glass, dried overnight at room temperature in a fume hood, and removed to a vacuum oven. The films were hung in the vacuum oven and dried at 30° C. for 72 hours. GPC analysis of the vacuum-dried films showed measured lactide levels of 0.0, 0.0, 0.4, 0.7 and 3.7 wt percent.

The films were then tested for film modulus using ASTM procedure D882.

The results are shown below in Table 20.

                  TABLE 20                                                         ______________________________________                                                                            Elastic                                     %     Tensile  Std.   %       Std. Modulus                                                                               Std.                                 Lactide                                                                              (psi avg.)                                                                              Dev.   Elongation                                                                             Dev. (psi avg.)                                                                            Dev.                                 ______________________________________                                         0     5490     636    2.85    0.14 730,000                                                                               103,000                              0     6070     123    2.85    0.22 818,000                                                                               35,000                               0.4   5670     227    2.75    0.27 779,000                                                                               44,000                               0.7   5690     343    4.04    1.12 749,000                                                                               58,000                               3.7   5570     458    3.33    1.43 738,000                                                                               66,000                               ______________________________________                                    

EXAMPLE 17

Rate of Water Uptake Versus Optical Composition

Samples of poly(lactide), made from 80 percent L-lactide and 20 percent of either D,L-lactide or meso-lactide, were ground to pass a 20 mesh screen. The samples were dried and devolatilized under vacuum then removed to a constant humidity chamber maintained at 24° C. and 50 percent relative humidity. The rate of moisture pick-up was determined gravimetrically, with the final results verified by Karl-Fischer water analysis. The rate of moisture pickup is shown below in Table 21.

                  TABLE 21                                                         ______________________________________                                                             Parts Per Million                                          Time                Weight Gain                                                (Minutes)           L/D,L Polymer                                                                              L/Meso Polymer                                 ______________________________________                                         10                   600        1000                                           30                  1100        1500                                           60                  1500        1800                                           120                 1600        2100                                           870                 2100        2600                                           Final   (Karl-Fischer)                                                                             3000        2600                                           ______________________________________                                    

EXAMPLE 18

Standard Test of Melt Stability

A standard test for determining melt stability is as follows:

A small sample (200 grams or less) of polymer is ground or pelletized and devolatilized by holding under vacuum (about 10 mm Hg) at a temperature of 130° C. or less for 18 hours. At this point the residual lactide content should be 1 wt percent or less. Portions (1-5 grams) of the devolatilized sample are then placed in a 16 ml sample vial, tightly capped, and placed in a 180° C. oil bath. Samples are removed at times of 15 minutes and 1 hour and analyzed for lactide content by GPC or other appropriate techniques. Lactide which may collect on the cooler portions of the vial is included in the product work-up and test.

Melt-stabilized poly(lactide) will show less than 2 percent lactide in the 15 minute sample, and more preferably less than 2 percent lactide in the 1 hour sample. The most highly stabilized poly(lactide)s will maintain lactide contents of less than 1 percent in both the 15 minute and 1 hour samples, preferably less than 0.5 percent. An unstabilized poly(lactide) may reach the equilibrium lactide content at 180° C. of 3.6 wt percent, or may go even higher as lactide is driven from the polymer melt and collects on the cooler top walls of the vial.

EXAMPLE 19

Water Scavenger Experiments

Dried poly(lactide) pellets were processed in a twin screw extruder to devolatilize and to prepare a portion with 0.5 percent by weight of a water scavenger (Stabaxol® P). The strands leaving the extruder are cooled in a water trough and chopped into pellets. Samples of the control and the test sample were then analyzed by the Karl Fischer technique for moisture content, with no drying. The control sample contained 1700 ppm water, the test sample had 450 ppm water. The control sample was then dried under nitrogen at 40° C., reducing the water content to 306 ppm. A vacuum-dried control sample had 700 ppm water.

The as-produced test sample and the dried control samples were then processed in a 1/2" single screw extruder (Brabender®) at 160° C., with a retention time of 3 minutes. The number average molecular weight for the dried control sample dropped from an initial value of 44,000 to a final value of 33,000 for the 306 ppm water sample and to 28,000 for the 700 ppm water sample. The test sample number average molecular weight dropped from an initial value of 40,000 to a final value of 33,000.

This sample shows how the water scavenger protected the polymer from moisture pick-up, imparting the same stability as a thorough drying of the control sample. Combining a water scavenger with appropriate drying is expected to give even greater stability.

EXAMPLE 20

Optimization of Catalyst Concentration

A mixture of 80 percent L-lactide and 20 percent D,L-lactide was polymerized using three different levels of tin(II) bis(2-ethyl hexanoate) catalyst. Batches were prepared at initial monomer/catalyst molar ratios of 1000:1, 3000:1, and 20,000:1. Polymerization times were adjusted to reach high conversion without being excessively long and thereby causing degradation in the melt. The reaction times were 1,2 and 20 hours, respectively. The polymerization temperature was 180° C. The polymers were ground to a coarse powder and devolatilized at 125° C. and 10 mm Hg overnight. The samples were then reground and 1-gram portions of each were placed into silanized vials, 16 ml capacity. The vials were sealed and placed into an oil bath at 180° C. Vials were then removed at various times and the samples were analyzed by GPC after dissolution in chloroform. The molecular weights and lactide contents are shown below in Table 22.

                  TABLE 22                                                         ______________________________________                                                Time   Number Average                                                                              Weight Average                                                                            Lactide                                  Sample (min)  Molecular Weight                                                                            Molecular Weight                                                                          Weight %                                 ______________________________________                                         1000:1 0      39,000       81,300     0.8                                             5      28,100       57,300     2.4                                             15     25,800       49,700     2.8                                             30     23,100       43,800     3.7                                             60     22,800       43,200     3.6                                      3000:1 0      53,100       113,600    0.6                                             5      39,000       76,400     0.4                                             15     30,300       65,400     1.9                                             30     29,000       60,400     2.7                                             60     28,200       55,200     2.8                                      20000:1                                                                               0      89,200       184,000    0.0                                             5      81,200       165,100    0.0                                             15     54,300       134,600    0.1                                             30     51,100       119,600    0.0                                             60     49,500       111,000    0.0                                      ______________________________________                                    

These results show the benefit of optimizing the catalyst level used in the polymerization process. Note that both lactide reformation and molecular weight retention benefits are realized from the reduced catalyst levels (higher monomer/catalyst ratio).

It is believed catalyst levels should be limited to 1000:1 for the high end of catalyst usage, with 3000:1 being more preferable and showing somewhat improved stability. Lower levels still, such as 20000:1, show greatly improved stability. Beyond this level it is believed the polymerization rates become too slow to be practical.

EXAMPLE 21

Removal of Tin Catalyst from Poly(lactide) by Precipitation

45 grams of L-lactide and 13 grams of D,L-lactide were charged with 78 milligrams of crystalline lactic acid to a 200 ml round bottom flask. This was heated to 180° C. with magnetic stirring in an oil bath and blanketed with dry nitrogen. Catalyst in the form of tin(II) bis(2-ethyl hexanoate) was added as 0.20 ml of a 0.47 g/ml solution in THF after the molten lactide was at temperature. The mixture was allowed to stir for one minute and then pipetted into 3 silanized glass vials, which were then sealed and placed into a 180° C. oil bath for 75 minutes. The vials were allowed to cool and the polymer recovered by breaking the glass. The polymer was ground to a coarse powder and dissolved in chloroform to make a 10 percent solution. The polymer contained 3.8 percent residual monomer and had a number average molecular weight of 70,000 as determined by GPC measurement (the method of Example 7)

500 ml of methanol were placed in a 1-liter glass blender flask. The blender was turned on to medium speed and 50 ml of the polymer in chloroform solution was poured in over a period of three minutes. After one additional minute of blending the mixture was filtered, then rinsed with 100 ml of methanol, and dried overnight under vacuum. The polymer consisted of a fibrous mat. It contained 0.3 percent residual monomer and had a number average molecular weight of 66,900.

The measured tin level in the precipitated polymer was 337 ppm by weight, compared to a calculated value of 466 ppm for the as-produced polymer. This result indicates the feasibility of reducing residual catalyst levels in lactide polymers by solvent precipitation with the benefit of improved stability as detailed in Example 20.

EXAMPLE 22

Shear Rate

Samples of devolatilized poly(lactide) were tested in a Rosand Model 14° C. capillary rheometer. The die was 1 mm diameter and 16 mm long, with an entry angle of 180 degrees. The table below gives the pressure drop across the die as a function of nominal shear rate (not Rabinowitsch corrected) for various molecular weights and temperatures.

                  TABLE 23                                                         ______________________________________                                                                      Nominal                                                                               Pressure                                                                shear rate                                                                            Drop                                       Mn       MW      Temp. (°C.)                                                                         (s.sup.-1)                                                                            (MPa)                                      ______________________________________                                         Results at 150° C.                                                       34,000   70,000 150         192    2.0                                                                     384    5.5                                                                     960    10.0                                                                    1920   13.8                                                                    4800   19.7                                                                    9600   23.7                                        52,000  108,000 150         192    9.9                                                                     384    15.6                                                                    960    19.9                                                                    1920   23.9                                                                    4800   29.4                                                                    9600   --                                          60,000  137,000 150         192    7.4                                                                     384    11.1                                                                    960    16.6                                                                    1920   21.0                                                                    4800   --                                                                      9600   --                                         183,000  475,000 150         192    19.1                                                                    384    27.0                                                                    960    31.4                                                                    1920   --                                                                      4800   --                                                                      9600   --                                         Results at 175° C.                                                       34,000   70,000 175         192    0.4                                                                     384    0.5                                                                     960    3.4                                                                     1920   5.5                                                                     4800   9.2                                                                     9600   12.5                                        52,000  108,000 175         192    2.2                                                                     384    4.6                                                                     960    7.6                                                                     1920   11.5                                                                    4800   17.2                                                                    9600   22.1                                       183,000  475,000 175         192    11.5                                                                    384    16.6                                                                    960    20.2                                                                    1920   24.4                                                                    4800   29.9                                                                    9600   --                                         Results at 200° C.                                                       60,000  137,000 200         192    0.5                                                                     384    1.6                                                                     960    3.3                                                                     1920   5.3                                                                     4800   --                                                                      9600   13.2                                       183,000  475,000 200         192    7.0                                                                     384    11.0                                                                    960    14.2                                                                    1920   17.9                                                                    4800   21.6                                                                    9600   --                                         ______________________________________                                    

EXAMPLE 23

Effect of Meso-lactide Concentration on Rate of Crystallization

Polymer samples of various optical compositions were prepared by polymerizing mixtures of L-lactide and meso-lactide with tin(II)bis(2-ethyl hexanoate) catalyst at a temperature of about 180° C. A portion of each sample was tested in a Mettler Differential Scanning Calorimeter (DSC), Model 30, by heating from 60° C. to 200° C. at 20° C./minute. The sample was then held at 200° C. for 2 minutes to completely melt any crystals. The samples were then quenched to the annealing temperature of interest and held 15 minutes. The samples were then quenched to 60° C. and reheated at 20° C./minute to 200° C. to determine the crystallinity. The crystallinity of the sample following annealing is proportional to the energy of the melting endotherm minus any crystallization exotherm.

                  TABLE 24                                                         ______________________________________                                         Net endotherm following 15 minut annealing                                     at given temperature (J/gm)                                                    Sample       Temperature =                                                                             Temperature =                                          (% meso)     85 ° C.                                                                            110° C.                                         ______________________________________                                         0            34.3       48.4                                                   3            5.1        48.2                                                   6            0.1        14.5                                                   9            0.3        11.0                                                   ______________________________________                                    

The results show that introducing meso-lactide greatly reduces the rate of crystallization for poly(lactide). Therefore, control of the meso level and tailoring the processing conditions are important.

EXAMPLE 24

The Effect of Meso-lactide Concentration on Crystallization

Samples of devolatilized poly(lactide) of varying optical composition and with number average molecular weights in the range of 50,000 to 130,000 were prepared in a continuous pilot plant. The samples were dissolved in chloroform to a concentration of 5 grams/100 cc and the optical rotation of the samples was measured to determine the concentration of meso-lactide which had been present in the monomer mixture prior to polymerization. Separate optical rotation and gas chromatography analysis of the monomer mixture confirmed that L-lactide and meso-lactide are the predominate components when meso-lactide is present at a concentration of 20 percent or less, and only a small correction is required for D-lactide.

Additional samples were made by polymerizing mixtures with known weights of L-lactide and meso-lactide.

All samples were subjected to an annealing procedure to develop crystallinity. The annealing procedure consisted of placing the samples in an oven at 100°-105° C. for 90 minutes, then lowering the temperature 10° C. each 1/2 hour until the temperature reached 45° C. The oven was then shut off and the samples were allowed to cool to room temperature. The energy of the melting endotherm and the peak melting temperature were then measured using a Mettler Differential Scanning Calorimeter (DSC) apparatus with a scan speed of 20° C./minute. The energy of melting is a measure of crystallinity in the annealed samples.

FIG. 3 shows sharp decline in crystallinity between 9 and 12 percent meso content.

EXAMPLE 25

Effect of Plasticizer on Crystallization Rate

Devolatilized polymer samples from a continuous pilot plant were compounded with dioctyl adipate (a plasticizing agent) and/or silica in a twin screw extruder. The samples were then tested from crystallization rate using the DSC of Example 23. In this case the DSC program included a first upheat, in which the samples were heated from -20° C. to 200° C. at a rate of 20° C./minute, holding at 200° C. for 2minutes, quenching, and a second upheat from -20° C. to 200° C at 20° C./minute. The energy of the crystallization exotherm, occurring at a temperature from about 75° C. to about 115° C., is proportional to the amount of crystallization which occurs during this two minute period.

The table below shows the increased crystallization observed when the plasticizer dioctyl adipate (DOA) is present, either with or without silica present. The base polymer, without plasticizer, shows no crystallization during the DSC upheat. The exotherms are reported on a joules per gram of poly(lactide) basis (filler free basis).

                  TABLE 25                                                         ______________________________________                                                      First Upheat                                                                               Second Upheat                                         Sample       Exotherm (J/gm)                                                                            Exotherm (J/gm)                                       ______________________________________                                         Base polymer 0           0                                                     Base polymer +                                                                              26.7        27.2                                                  8 wt % DOA                                                                     Base polymer +                                                                              4.0         0                                                     40 wt % silica                                                                 Base polymer +                                                                              27.1        27.6                                                  40 wt % silica +                                                               5 wt % DOA                                                                     ______________________________________                                    

EXAMPLE 26

An Evaluation of Nucleating Agents

A devolatilized sample of poly(lactide) polymer was compounded with a variety of potential nucleating agents in a single screw extruder. The candidate nucleating agents were added at a nominal level of 5 percent by weight. The single screw extruder is not as effective of a mixer as would be used commercially, so failure to observe an effect in these tests does not mean that a candidate agent would not be effective if blended more thoroughly. A positive result in this test demonstrates potential ability to increase crystallization rates. Additives which increased crystallinity in the second upheat (on a quenched sample) were rated ++, additives which showed an effect only on the first upheat were rated +, and additives which showed no effect were rated 0.

                  TABLE 26                                                         ______________________________________                                         Additive               Effect                                                  ______________________________________                                         None                   0                                                       talc, MP1250 (Pfizer)  ++                                                      3-nitro benzoic acid   0                                                       saccharin, sodium salt ++                                                      terephthalic acid,     0                                                       disodium salt                                                                  calcium silicate, -200 mesh                                                                           +                                                       sodium benzoate        +                                                       calcium titanate, -325 mesh                                                                           +                                                       boron nitride          +                                                       calcium carbonate, 0.7 micron                                                                         0                                                       copper phthalocyanine  +                                                       saccharin              0                                                       low molecular weight polyethylene                                                                     0                                                       talc, Microtuff-F (Pfizer)                                                                            ++                                                      talc, Ultratalc (Pfizer)                                                                              ++                                                      ethylene acrylic acid sodium ionomer                                                                  0                                                       (Allied Signal)                                                                isotactic polypropylene                                                                               +                                                       polyethylene terephthalate                                                                            0                                                       crystalline poly(L-lactide) (low mol. wt.)                                                            ++                                                      Millad 3940 (Milliken) ++                                                      Millad 3905 (Milliken) +                                                       NC-4 (Mitsui)          +                                                       polybutylene terephthalate                                                                            +                                                       talc in polystyrene (Polycom Huntsman)                                                                +                                                       talc in polyethylene (Advanced                                                                        ++                                                      Compounding)                                                                   ______________________________________                                    

EXAMPLE 27

Heat Set Crystallization of an Oriented Poly(lactide) Film

Two film samples, one non-oriented and the other biaxially oriented, were constrained in a film holder and annealed for either 5 minutes or 15 minutes in an oil bath at 85° C. The extent of crystallization was determined by DSC from the melting endotherm of the crystalline domains formed during the annealing, using a ramp rate of 20° C./minute. The biaxially oriented film developed significantly more crystallinity for each time, as shown in the table below.

                  TABLE 27                                                         ______________________________________                                                t = 0 minutes                                                                               t = 5 minutes                                                                              t = 15 minutes                                 Sample endotherm(J/gm)                                                                             endotherm(J/gm)                                                                            endotherm(J/gm)                                ______________________________________                                         non-   0.6          0.0         0.8                                            oriented                                                                       biaxially                                                                             0.7          8.1         8.5                                            oriented                                                                       ______________________________________                                    

Each of the films was made from lactide mixtures containing an estimated meso-lactide content of about 12 wt %, with about 88 wt % L-lactide. When subjected to the slow oven annealing procedure of Example 24, samples from both of the films developed crystallinity which gave a melting endotherm of about 25 J/gm. The biaxially oriented film had been stretched approximately 4× in the machine direction and 2× in the transverse direction (using a tenter frame), all at about 63°-74° C.

EXAMPLE 28

Properties of PLA-cellulose Acetate Blends

In the twin screw extruder described in Example 1, poly(lactide) was blended with cellulose acetate (Tenite 110 from Eastman), cellulose acetate propionate (Tenite 375 from Eastman), and cellulose butyrate (Tenite 575 from Eastman) in levels shown in Table 28. The poly(lactide) had a weight average molecular weight of about 200,000, a meso content of about 10.5%, a residual lactide level of about 0.3%, and a moisture content less than about 300 ppm. The weight percentages of poly(lactide) and cellulose derivatives is shown in the following table:

                                      TABLE 28                                     __________________________________________________________________________     Composition                                                                           1  2  3  4  5  6  7  8  9  10                                           __________________________________________________________________________     CA        20%                                                                               50%                                                                               80%                                                            CAP                20%                                                                               50%                                                                               80%                                                   CAB                         20%                                                                               50%                                                                               80%                                          PLA    100%                                                                              80%                                                                               50%                                                                               20%                                                                               80%                                                                               50%                                                                               20%                                                                               80%                                                                               50%                                                                               20%                                          __________________________________________________________________________

The blends were prepared using a melt temperature of 190°-200° C., die pressure of 18-20 bar, and a screw speed of 250 rpm. All materials but one were pelletized, dried and injection molded into a standard ASTM test specimen mold for testing. Composition 3 was not pelletized due to poor strength of the extruded polymer stand. This is evidence of mechanical incompatibility of the cellulose acetate and poly(lactide). The remaining compositions were tested for tensile strength and elongation to break in accord with ASTM D 638-91 and heat distortion temperature according to ASTM D 648-82.

Another test performed on each sample was a test for resistance to hot water. A standard tensile bar is placed in a hot water bath at 190° F. for 3 minutes. The sample is removed from the water and placed in a horizontal position with the flat sides facing up and down with one end of the tensile bar held in a clamp. Samples which have softened as a result of the hot water exposure will bend under the force of gravity. The degree of bend is measured using a protractor. The maximum degree of bend is 90° and constitutes a failure. The best result is no bend of the sample.

The test results are shown in the following table:

                  TABLE 29                                                         ______________________________________                                               Tensile   Elongation         Hot water test                                    strength  to       Heat distortion                                                                          angle of                                    Sample                                                                               to break (psi)                                                                           break (%)                                                                               temperature (°C.)                                                                 (deformation)                               ______________________________________                                         1     7100      5.4      51.1      46°                                  2     5900      1.5      41.7      44°                                  3     --        --       --        --                                          4 10  3200      2.2      --        0°                                   5     8100      2.2      46.7      10°                                  6     5600      6.9      45.7      3°                                   7     4700      17.9     50.0      0°                                   8     7600      2.3      48.2      23°                                  9 15  5500      8.3      --        0°                                   10    5100      17.9     51.9      0°                                   ______________________________________                                    

These results show that many compositions of poly(lactide) blended with CA, CAP and CAB are compatible enough to exhibit good physical properties. Blends of PLA with high loadings of CAP and CAB may increase the flexibility of unblended poly(lactide). Resistance of poly(lactide) to hot water was dramatically increased by addition of CA, CAP or CAB.

EXAMPLE 29

Heat Sealability of a Poly(lactide) Film

Poly(lactide) with a weight average MW of 160,000, a meso content of 8 to 12%, and a moisture level of about 200 ppm was extruded into film using the same method as Example 2.

Two pieces of the poly(lactide) film were heat sealed in an Accuseal Heat Sealer Model 30 having heated platens of a dimension of 1/4"×25". The temperature and dwell time were varied to find the minimum time required to form a bond between the films. The pressure was 40 psi. Bond strength was estimated by pulling the two films apart 10 seconds after sealing and judging pass or fail. Either the films tore before the bond failed (pass) or the films separated at the bondline (fail). Results are shown below:

                  TABLE 29                                                         ______________________________________                                         Time  Temperature (C°)                                                  (sec) 30     40     50  60   65  70   75  80   85   90                         ______________________________________                                         1     F      F                                                                 2                   F   F    F   F    F                                        3                       F                 P    P                               4                            P                      P                          5                                     P                                        6                                                   P                          ______________________________________                                    

Sealing conditions of 70° C. at a line pressure of 40 psi for a 2 second dwell time were found to be sufficient for forming a good bond between the two poly(lactide) films.

EXAMPLE 30

Effect of Talc on Crystallization Rate of Poly(lactide)

Poly(lactide) prepared in a continuous pilot plant, from a lactide mixture with an approximate composition of 91% L-lactide and 9% meso-lactide, was dried and devolatilized in a twin screw extruder. The polymer was then redried and talc (Ultratalc 609, from Pfizer) was compounded in at levels from 2 wt % to 21 wt %.

Samples of the compounded poly(lactide) were placed in a DSC apparatus and subjected to a heating program consisting of a first upheat from 60° C. to 200° C. for two minutes, quenching to 90° C., holding at 90° C. for 15 minutes, followed by a quench and second upheat from 60° C. to 200° C. The first upheat and quench is to make each of the samples amorphous, the crystallization exotherm is measured during the 90° C. isothermal run, and the second upheat is used to confirm the isothermal exotherm through a direct measurement of the melting endotherm of the crystalline domains formed during the isothermal annealing.

The table below shows the extent of crystallization (reported on talc free basis) as a function of time for various talc loadings. The results show that talc significantly increases the rate of crystallization of the poly(lactide).

                                      TABLE 30                                     __________________________________________________________________________               Exotherm (J/gm of PLA) to time                                                                       2nd upheat                                     Sample    2 min.                                                                             5 min.                                                                              8 min.                                                                             12 min.                                                                             15 min.                                                                            J/gm)                                          __________________________________________________________________________     PLA       0   0    0   0    0   0                                              PLA + 2 wt % talc                                                                        0.1 0.6  1.1 4.2  7.9 10.0                                           PLA + 6 wt % talc                                                                        0.5 2.6  5.3 11.8 17.2                                                                               21.2                                           PLA + 11 wt % talc                                                                       0.8 2.5  10.8                                                                               22.2 27.3                                                                               28.2                                           PLA + 21 wt % talc                                                                       2.3 11.3 19.2                                                                               25.4 27.6                                                                               26.2                                           __________________________________________________________________________

EXAMPLE 31

Stress-induced Crystallization of a Poly(lactide) Sheet

Poly(lactide), copolymerized with 0.55 wt % epoxidized linseed oil, from a continuous pilot plant was dried, devolatilized, redried, and compounded with 25 wt % talc (Ultratalc 609, Pfizer) and 25 wt % plasticizer (Citroflex A-4, Morflex). This material was then dried and cast into a 15 mil sheet. Strips of the sheet, approximate 1"×4", were loaded into an MTS test instrument using a 1" gap width and stretched to about 4× at room temperature. After stretching, the test samples were removed from the MTS and analyzed by a DSC to determine the amount of stress-induced crystallization, using the net melting endotherm. Crystallization exotherms were not observed for these samples, except for the unstretched control.

                  TABLE 31                                                         ______________________________________                                         Sample (stretching speed)                                                                         Melting endotherm (J/gm)                                    ______________________________________                                         unstretched (control)                                                                             2.4 (net, after subtracting                                                    crystallization exotherm)                                    5 mm/sec (nominal)                                                                               19.1                                                        26 mm/sec (estimated)                                                                             17.3                                                        26 mm/sec (estimated)                                                                             19.2                                                        26 mm/sec (estimated)                                                                             17.5                                                        26 mm/sec (estimated)                                                                             18.3 (sample tore at end of                                                    test)                                                       ______________________________________                                    

Each of the stretched samples showed a pronounced development of stress-included crystallization.

EXAMPLE 32

Stress-induced Crystallization of a Poly(lactide) Film

Poly(lactide), copolymerized with 0.55 wt % epoxidized linseed oil, was dried, devolatilized, and redried. The lactide had a meso-lactide content of about 8-10%. The material was then cast into 15 mil sheet. Squares of the material, approximately 5"×5", were stretched using an Iwamoto biaxial stretcher either in a single direction or biaxially. The stretching temperature was 65° C. and the stretching speed was 10 mm/s. The stretched films were tested by DSC to determine the extent of crystallization.

                  TABLE 32                                                         ______________________________________                                                 Cold Crystallization                                                                           Melting     Net                                        Sample  Exotherm (J/gm) Endotherm (J/gm)                                                                           J/gm                                       ______________________________________                                         1 × 2                                                                            1.2             1.7         0.5                                        1 × 3                                                                            16.4            23.7        7.3                                        1 × 4                                                                            12.6            19.9        7.3                                        4 × 4                                                                            17.7            22.6        4.9                                        ______________________________________                                    

EXAMPLE 33

Heat-set Crystallization of an Oriented Poly(lactide Film

The biaxially oriented sample (4×4) of Example 32 was constrained in a film holder and annealed at 85° C. for one minute. The annealed sample had a cold crystallization exotherm of 1.3 J/gm, a melting endotherm of 21.6 J/gm, and a net endotherm of 20.3 J/gm. For comparison, Example 23 shows that a non-oriented sample of comparable meso content has a net endotherm of less than 1 J/gm after 15 minutes of annealing at 85° C.

EXAMPLE 34

Crystallization of Pellets and Films During Storage

The talc filled, plasticized, pellets and unoriented films of Example 31 were stored at room temperature for 12 days and 11 days, respectively They were then retested by DSC to determine if any crystallization had taken place during storage. Significant crystallization had occurred, and the feed pellets showed a melting endotherm of 17.4 J/gm and the film showed a melting endotherm of 18.8 J/gm on an as-tested basis. This corresponds to 35 J/gm and 38 J/gm on a poly(lactide) basis. No crystallization exotherms were observed during the DSC upheat.

EXAMPLE 35

Stress-induced Crystallization and Strain Hardening of a Poly(lactide) Film

Additional samples of the polymer film used in Example 32 were subjected to uniaxial stretching on the Iwamoto biaxial stretcher. The polymer, after melting and quenching, exhibited a Tg with an inflection point of 59° C. when tested by DSC at a scan rate of 20° C./min. The samples were stretched at various temperatures at a rate of 99 mm/sec and tested by DSC to determine the extent of crystallization. Force curves for the stretching operation were also recorded.

                  TABLE 33                                                         ______________________________________                                                                Stretching Force (kg) needed                            Stretching Net Melting at elongation of                                        Temperature (°C.)                                                                  Endotherm (J/gm)                                                                           initial 200%  300% 400%                                 ______________________________________                                         68         18          28      24    27   49                                   72         18          26      30    40   52                                   76         20          14      14    14   16                                   80          8          11      11    12   16                                   ______________________________________                                    

The table above shows the development of stress induced crystallinity when the polymer was stretched at temperatures up to 20° C. above Tg. At 80° C. less stress induced crystallinity developed, although the sample crystallized readily during subsequent annealing. The samples stretched at 68° C. and 72° C. show pronounced strain hardening at 300-400% elongation during this test. The samples stretched at higher temperatures did not show the same degree of strain hardening.

It will be understood that even though these numerous characteristics and advantages of the invention have been set forth in the foregoing description, together with details of the structure and function of the invention, the disclosure is illustrative only, and changes may be made in detail, especially in matters of shape, size and arrangement of the parts or in the sequence or the timing of the steps, within the broad principle of the present invention to the full extent indicated by the broad general meaning of the terms in which the appended claims are expressed. 

What is claimed:
 1. A film having a net endotherm greater than about 10 joules per gram of polymer that contains chains including lactic acid residuals;-said film further comprising:(a) a melt stable polymer composition including at least 5%, by weight, of a melt stable first polymer component including polymer chains with at least lactic acid residuals, based on total weight of melt stable polymer in said melt stable polymer composition;(i) said first polymer component being formed from at least:(A) a source of (R)-lactic acid residuals; and (B) a source of (S)-lactic acid residuals; (ii) said first polymer component having (R)-lactic acid residuals and (S)-lactic acid residuals in a distribution in the polymer such that sequences of a major lactic acid residual have at least a 0.5 probability of including a sequence of at least 10 of the major lactic acid residuals consecutively; (b) said first polymer component having a number average molecular weight of at least 40,000 and no greater than about 300,000; and, (c) said first melt stable polymer composition having a lactide concentration, if present at all, of less than about 2% by weight of melt stable polymer including polymer chains with lactic acid residuals, in said first polymer component; (d) said melt stable first polymer component being a material in a form sufficiently melt stable such that a devolatized sample of it, when isolated and prior to formation of said melt stable polymer composition, will show formation of less than 1% lactide presence, by weight, after heating for 1 hour at 180° C.
 2. A film according to claim 1 wherein:(a) said source of (R)-lactic acid residuals from which said first polymer component is formed includes meso-lactide; and (b) said source of (S)-lactic residuals from which said first polymer component is formed also includes meso-lactide and further includes L-lactide.
 3. A film according to claim 2 wherein:(a) said source of (R)-lactic acid residuals further includes D-lactide.
 4. A film according to claim 2 wherein:(a) L-lactide comprises at least 85%, by weight, of the combined presence of said sources of (R)-lactic acid residuals and (S)-lactic acid residuals.
 5. A film according to claim 4 wherein:(a) said first polymer component includes residual in the polymer chains in addition to said lactic acid residuals.
 6. A film according to claim 5 wherein:(a) said residual in the polymer chains in addition to lactic acid residuals comprises diol residual.
 7. A film according to claim 5 wherein:(a) said residual in the polymer chains in addition to lactic acid residuals comprises triol residual.
 8. A film according to claim 5 wherein:(a) said residual in the polymer chains in addition to lactic acid residuals comprise residual of material having more than one group reactive for incorporation into the polymer chains.
 9. A film according to claim 8 wherein:(a) said material having more than one group reactive for incorporation into the polymer chains has at least three sites for incorporation into the polymer chains.
 10. A film according to claim 9 wherein:(a) said material having more than one group reactive for incorporation into the polymer chains, and having at least three sites for incorporation into the polymer chains, is a triol.
 11. A film according to claim 2 wherein:(a) said polymer chains of said first polymer component also include residual formed as a result of reacting an epoxide into the polymer.
 12. A film according to claim 1 wherein:(a) said first polymer component is formed from at least:meso-lactide, L-lactide and epoxidized oil.
 13. A film according to claim 1 is wherein:(a) said melt stable polymer composition comprises a polymer blend of the first polymer component with a second polymer that does not contain lactic acid residuals.
 14. A film according to claim 13 wherein:(a) said second polymer in said polymer blend is selected from the group consisting of: aliphatic polyesters, aliphatic polyamides, esterified cellulose resins, modified starch, polyvinyl acetate, polyvinyl alcohol, polyethers, polycarbonates, polyurethanes, polyanhydrides, natural rubber, epoxidized natural rubber, block copolymers of styrene and isoprene, block copolymers of styrene and butadiene, polyacrylates, polymethacrylates, polyolefins and polystyrene.
 15. A film according to claim 14 wherein:(a) said second polymer is an aliphatic polyester.
 16. A film according to claim 1 wherein:(a) said melt stable first polymer component has a water concentration, if water is present at all, of less than about 500 parts per million.
 17. A film according to claim 1 wherein:(a) said first polymer component is formed from at least:meso-lactide, L-lactide, epoxidized oil and antioxidant.
 18. A film according to claim 1 wherein:(a) said first polymer component is formed from at least:meso-lactide, L-lactide, epoxidized oil and catalyst deactivating agent.
 19. An article including a film wherein:(a) said film has a net endotherm greater than about 10 joules per gram of polymer component therein having polymer chains with lactic acid residuals; said film comprising a melt stable polymer composition including at least 5 by weight of a melt stable first polymer component including polymer chains with at least lactic acid residuals, based on total weight of polymer in said melt stable polymer composition;(i) said first polymer component being formed from at least:(A) a source of (R)-lactic acid residuals; and (B) a source of (S)-lactic acid residuals; (ii) said first polymer component having (R)-lactic acid residuals and (S)-lactic acid residuals in a distribution in the polymer such that sequences of a major lactic acid residual have at least a 0.5 probability of including a sequence of at least 10 of the major lactic acid residuals consecutively; (b) said first polymer component having a number average molecular weight of at least 40,000 and no greater than about 300,000; and, (c) said first melt stable polymer composition having a lactide concentration, if present at all, of less than about 2% by weight of melt stable polymer including polymer chains with lactic acid residuals in said first polymer component; (d) said melt stable first polymer component being a material in a form sufficiently melt stable such that a devolatized sample of it, when isolated and prior to formation of said melt stable polymer composition, will show formation of less than 1% lactide presence, by weight, after heating for 1 hour at 180° C.
 20. An article according to claim 19 wherein:(a) said first polymer component includes residual within the polymer chains in addition to lactic acid residuals.
 21. An article according to claim 19 comprising a packaging film.
 22. An article according to claim 19 comprising a bag.
 23. A film having a net endotherm greater than about 10 joules per gram of polymer that contains chains including lactic acid residuals; said film further comprising:(a) a melt stable polymer composition including at least 5%, by weight, of a melt stable first polymer component including polymer chains with at least lactic acid residuals, based on total weight of melt stable polymer in said melt stable polymer composition;(i) said first polymer component comprising polymer chains comprising at least 85% by weight residues selected from the group consisting essentially of L-lactide, D-lactide, and mixtures thereof; and (ii) said first polymer component having (R)-lactic acid residuals and (S)-lactic acid residuals in a distribution in the polymer such that sequences of a major lactic acid residual have at least a 0.5 probability of including a sequence of at least 10 of the major lactic acid residuals consecutively; (b) said first polymer component having a number average molecular weight of at least 40,000 and no greater than about 300,000; and, (c) said first melt stable polymer composition having a lactide concentration, if present at all, of less than about 2% by weight of melt stable polymer including polymer chains with lactic acid residuals, in said first polymer component; (d) said melt stable first polymer component being a material in a form sufficiently melt stable such that a devolatized sample of it, when isolated and prior to formation of said melt stable polymer composition, will show formation of less than 1% lactide presence, by weight, after heating for 1 hour at 180° C.
 24. A film according to claim 23 wherein:(a) said first polymer component includes residual in the polymer chains in addition to said lactic acid residuals.
 25. A film according to claim 24 wherein:(a) said residual in the polymer chains in addition to lactic acid residuals comprises diol residual.
 26. A film according to claim 23 wherein:(a) said polymer chains of said first polymer component also include residual formed as a result of reacting an epoxide into the polymer.
 27. A film according to claim 23 wherein:(a) said first polymer component is formed from at least:meso-lactide, L-lactide and epoxidized oil.
 28. A process of preparing a film having a net endotherm greater than about 10 joules per gram of polymer that contains chains including lactic acid residuals; said process including a step of:(a) extruding a melt stable polymer composition including at least 50, by weight, of a melt stable first polymer component including polymer chains with at least lactic acid residuals, based on total weight of melt stable polymer in said melt stable polymer composition;(i) said first polymer component being formed from at least:(A) a source of (R)-lactic acid residuals; and (B) a source of (S)-lactic acid residuals; (ii) said first polymer component having (R)-lactic acid residuals and (S)-lactic acid residuals in a distribution in the polymer such that sequences of a major lactic acid residual have at least a 0.5 probability of including a sequence of at least 10 of the major lactic acid residuals consecutively; (b) said first polymer component having a number average molecular weight of at least 40,000 and no greater than about 300,000; and, (c) said first melt stable polymer composition having a lactide concentration, if present at all, of less than about 2% by weight of melt stable polymer including polymer chains with lactic acid residuals, in said first polymer component; (d) said melt stable first polymer component being a material in a form sufficiently melt stable such that a devolatized sample of it, when isolated and prior to formation of said melt stable polymer composition, will show formation of less than 1% lactide presence, by weight, after heating for 1 hour at 180° C. 